刘茜
,
许钫钫
,
阮美玲
,
高濂
,
THOMPSON Derek P
,
温树林
无机材料学报
doi:10.3321/j.issn:1000-324X.1999.06.011
系统研究了通过外部添加增韧相和热处理诱发原位自增韧机制等工艺因素控制所引起的三种Sialon基陶瓷材料的显微结构变化及其对力学性能的影响.研究内容包括:1.TiN(p)、MoSi2(p)、SiC(p)和SiC(w)第二相物质复合Sialon陶瓷的界面结合状态及其增韧效果;2.利用Nd2O3、Dy2O3和Yb2O3典型稀土氧化物作为烧结添加剂,制备α/β两相复合Sialon材料,诱发β相长颗粒生长,导致类晶须长颗粒原位自增韧机制发生作用;3.α-Sialon长颗粒的成核及生长机制.研究结果表明:对于TiN(p)、MoSi2(p)、SiC(p)和SiC(w)第二相复合Sialon陶瓷,基质相与第二相的界面结合状态及第二相颗粒临界粒径是制约复相材料韧性的主要因素.对于Nd2O3、Dy2O3和Yb2O3典型稀土氧化物Sialon材料,轻稀土Nd2O3是良好的烧结助剂,且Nd-Sialon相变程度极高,热处理诱发大量长颗粒β-Sialon相生成是其具有高韧性的主要原因(最高断裂韧性值达7.0MPa·m1/2).重稀土Yb2O3不仅是良好的烧结助剂,同时也是有效的α-Sialon稳定剂,体系内存在大量等轴状α-Sialon颗粒,使此种材料硬度高达18.00GPa.中稀土Dy2O3的作用介于轻稀土Nd2O3和重稀土Yb2O3之间.α-Sialon长颗粒的特殊生长机理源于异相成核和各向异性外延生长二个过程.
关键词:
Sialon基陶瓷
,
第二相增韧
,
原位增韧
,
显微结构
,
力学性能
Materials Letters
The effects of P and B on the creep behavior of 718 alloys are discussed in this paper. The result implies that P and B have little effect on the gamma" and gamma' phases of the alloy, but they can enhance the grain boundary strength by segregating there, which can be of beneficial to the higher creep properties. P also may increase the grains strength through solid solution. The beneficial effect of P and B were presented in both standard IN718 alloy and DA718 alloy. Adding P and B together does a better work than adding P alone. (c) 2006 Elsevier B.V. All rights reserved.
关键词:
P and B;718 alloy;creep;grain boundaries;heat treatment;stress rupture;phosphorus;superalloy;boron
宿辉
,
蔡伟
,
曹茂盛
材料科学与工艺
doi:10.3969/j.issn.1005-0299.2008.03.004
为解决Ni-P-(SiC)P镀层中基体的金属键与增强体的共价键间相容性差,增强体颗粒易脱落,镀层性能降低等问题.采用简单的化学镀方法实现了(SiC)P表面修饰、改性,得到了涂覆型改性(Ni/SiC)P,以(Ni/SiC)P为第二相粒子制备了Ni-P-(Ni/SiC)P化学复合镀层,并初步分析了复合镀机理.实验结果表明:温度、pH值、搅拌速率及(Ni/SiC)P加入量对Ni-P-(Ni/SiC)P镀层的沉积速率及沉积量有较大的影响,本实验条件下的最佳温度为82~86℃;最佳pH值为4.2~4.6;最佳搅拌速率为200 r/mim;最佳粒子加入量10 g/L.SEM、EDS分析显示Ni-P-(Ni/SiC)P镀层均匀、致密,Ni、P、Si沉积量大,耐磨性实验证明Ni-P-(Ni/SiC)P化学复合镀层硬度、耐磨性优干常见的Ni-P、Ni-P-(SiC)P镀层.经表面修饰、改性后得到的(Ni/SiC)P可以进一步提高Ni-P-(SiC)P镀层的使用性能.
关键词:
化学镀
,
(Ni/SiC)P
,
镀层
,
工艺条件
,
耐磨性
宿辉
,
蔡伟
,
曹茂盛
材料工程
doi:10.3969/j.issn.1001-4381.2007.10.010
为解决裸(SiC)p在实际应用中存在的不足,采用简单的化学镀方法对其表面进行改性,得到了包覆型的改性(Ni/SiC)p,以(Ni/SiC)p为第二相粒子制备了Ni-P-(Ni/SiC)p化学复合镀层,经扫描电镜、能量散射仪、硬度等测试,并与常见的Ni-P化学镀层、Ni-P-(SiC)p化学复合镀层比较,结果显示:Ni-P-(Ni/SiC)p镀层具有组成均匀、硬度高、镀层耐磨损等优点,为(SiC)p增强金属镀层及基体材料的研究提供了一个新的思路.
关键词:
化学镀
,
(Ni/SiC)p
,
镀层
,
硬度
NING Hua ZHANG Lixin Institute of Corrosion and Protection of Metals
,
Academia Sinica
,
Shenyang
,
China
金属学报(英文版)
The segregation behaviour of P and its effect on structure of 70%-reduction cold rolled Fe-P alloys containing different contents of P,e.g.,0.007,0.06 and 0.09% P,during annealing at 200-700℃ under vacuum have been studied by means of metallography and EPMA.The P was found to segregate preferentially along dislocation line during recovery annealing.The P-riched dislocation densing region,the P-depleted region and the sub-grain-like boundary thus formed.The nuclei grow preferentially during recrystallization in such region that the P segregation is more evident and the residual strain by dislocation densing increases to large extent.After recrystallizing,the P segregates along grain boundaries and makes the grains in alloy fine. Engineer,Institute of Corrosion and Protection of Metals,Academia Sinica,Shenyang 110015,China
关键词:
P
,
null
,
null
,
null
韩其勇
,
张晓东
,
王鹏飞
,
王杰
,
陈冬
金属学报
用Ca与P合成的Ca_3P_2,在1600℃通过Ca_3P_2的分解,测定了纯Fe液中Ca-P平衡常数和活度相互作用系数,得到 K_(Ca_3P_2)=α_(Ca)~3·α_P~2=7.0×10~(-14) e_P~(Ca)=-3.1
关键词:
Ca-P平衡
,
Ca P
赵芳霞
,
刘琛
,
张振忠
,
丘泰
材料保护
doi:10.3969/j.issn.1001-1560.2006.03.020
利用SEM、DSC、XRD、中性盐雾试验和显微硬度分析等手段,对Ni-10.54%P及Ni-9.25%Cu-10.23%P化学镀层的组织特征、相结构转变、热稳定性、耐蚀性和硬度进行了比较.结果表明:(1)两种镀层均匀致密,均为胞状结构和非晶态组织;(2)Ni-P镀层仅发生从非晶相向稳定的Ni3P相转变,而Ni-Cu-P镀层则先生成Ni-Cu固溶体和亚稳中间相Ni5P2,再向稳定相Ni3P转变;(3)Ni-Cu-P镀层的热稳定性高于Ni-P镀层;(4)镀态和低温热处理条件下两种镀层的硬度相差不大,Ni-P镀层经400 ℃、60 min热处理时硬度达到最高值981.1 HV,但Ni-Cu-P镀层经500 ℃、60 min热处理时硬度达到最高值1 144.8 HV;(5)镀态时Ni-Cu-P镀层的腐蚀速率只有Ni-P镀层腐蚀速率的2.85%;经过400 ℃、120 min相同条件的热处理,Ni-Cu-P镀层的腐蚀速率仅为Ni-P镀层腐蚀速率的0.351%.
关键词:
化学镀
,
Ni-P
,
Ni-Cu-P
,
热稳定性
,
硬度
,
耐蚀性
ZHANG Lixin NING Hua Laboratory of Corrosion Science
,
Institute of Corrosion and Protection of Metals
,
Academia Sinica.Shenyang
,
ChinaZHOU Jing LI Liguang Institute of Metal Research
,
Academia Sinica
,
Shenyang
,
China Professor
,
Institute of Corrosion and Protection of Metals
,
Academia Sinica
,
Shenyang 110015
,
China
金属学报(英文版)
The relations between the non-equilibrium segregation process of P and the change of the texture in Fe-P alloys have been studied by analytical electron microscope and orientation distribution function.It was shown that P segregated preferentialy on the{110}slip planes, the P segregation structures with repeating cycle a=1.582 nm form at 450℃.<001>// ND direction abated.<111>//ND direction heightened.And{111}<110>has a tendancy to transform into{111}<143>texture in recovering process.{111}<143>direction trans- forms into{111}<112>direction after recrystalizing.A model to describe the effects of non-equilibrium segregation structures of P on orientation change was proposed and em- ployed to interpret the experiment results.
关键词:
Fe-P Alloy
,
null
,
null
,
null