金属学报(英文版)
An inflection hehaviour was revealed during isothermal annealing under the observation of transition of the coercivity of Fe-Si-B amorphous alloys during local crystallization.It may be interpreted by the transition of α-Fe grain precipitated from single to multiple domain, Thus,the theoretical expression of H_0-t_a may be derived.The plot of expression H_0-t_a calcu- lated well represents the feature of the experimental curve.
关键词:
Fe-base amorphous alloy
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,
null
,