ZHANG Jie
,
CAI Qing-wu
,
WU Hui-bin
,
ZHANG Kun
,
WU Bo
钢铁研究学报(英文版)
A new kind of Mn-Mo-Nb-Cu-B bainite steel which satisfied mechanical demands of E690 offshore plate steel was designed. The effect of two processes——thermomechanical control process (TMCP)+tempering (T) and thermomechanical control process (TMCP)+reheating and quenching (RQ)+tempering (T)——on microstructure and mechanical properties were studied by means of scan electron microscope (SEM), transmission electron microscope (TEM) and electron back scatter diffraction (EBSD). The results showed that optimal mechanical properties were available when tempering at 550 ℃ for both processes. The microstructure of the TMCP+T treated sample tempering in the range of 450 to 550 ℃ for 1 h did not change dramatically yet the lath in the TMCP+RQ+T treated sample merged together and transformed into polygonal ferrite. At the same time, the sub-structure of grain bainite transformed from lath to cell-shape to refine grains with tempering temperature mounting. Lots of sub-grain boundaries were located within bainite and adjacent bainite grain boundaries were high angle.
关键词:
offshore plate
,
low carbon bainitic steel
,
tempering
,
toughness
,
EBSD
YANG Guang-hui
,
CAO Jian-guo
,
ZHANG Jie
,
SONG Ping
,
YAN Tan-li
,
RAO Ke-feng
钢铁研究学报(英文版)
In order to solve the difficult profile and flatness control problem of wide non-oriented electrical steel sheets, the factors such as the relationship between strip crown control and strip width, the relationship between the maximum wearing value of work roll and the number of a rolling campaign and the wear contour change of work roll were analyzed on the basis of industrial test. Through analyzing the rolling process characteristics of non-oriented electrical steel sheets, the ASR (asymmetry self-compensating work rolls) shape control technology and its roll shifting strategy of the wider non-oriented electrical steel sheets was proposed and developed. When the technology was applied, the number of the wide non-oriented electrical steel (23 mm×1280 mm) in one rolling campaign rose from 40 coils of the trial production to 70 coils of the industrial production, the ratio of the measured strip crown less than 45 μm was increased from 500% to 949%, and the ratio of the measured strip crown more than 60 μm was decreased from 200% to 07%.
关键词:
silicon steel
,
shape control
,
hot rolling
,
roll contour
TIAN Li-li
,
Paolo Patrizi Jie
,
ZHANG Jie
钢铁研究学报(英文版)
In this paper we propose a new theoretical thermo-mechanical explanation of the uneven transverse temperature distribution, along the width, for thin and wide hot rolled produced strip. In particular, we base our reasoning starting from the irregular pressure/friction distribution, that lead to an uneven heat generation. A 2-D mathematical model to calculate the transverse temperature distribution is presented, both to give a physical explanation to our problem, and to be used as an essential basis to build a correspondent FEM simulation model, in which heat loss and generation are both considered. Deformation and friction heat are both described in details, having a paramount importance in our reasoning. The heat generation problem is split into two parts, for a clearer and more logical analysis: one for the strip centre, and one for the sides, in correspondence of the temperature peak points at 100mm from the strip edge. Finally it is shown how our new theoretical model can lead to the exact interpretation of the measured uneven temperature distribution.
关键词:
Hot strip rolling;Strip temperature distribution;Strip thermo-mechanical behaviour;Deformation heat;Friction heat
Journal of Materials Research
The morphology of the dark and bright regions observed by transmission electron microscopy for the Zr(64.13)Cu(15.75)Ni(10.12)Al(10) bulk metallic glass strongly depends on the ion beam parameters used for ion milling. This indicates that the ion beam could introduce surface fluctuation to metallic glasses during ion milling.
关键词:
room-temperature
Nuclear Engineering and Design
Liquid droplet erosion (LDE), which often occurs in bellows made of nickel-based alloys, threatens the security operation of the nuclear power plant. As the candidate materials of the bellows, Inconel 600 and Inconel 625 were both tested for resistance to cavitation erosion (CE) and jet impingement erosion (JIE) through vibratory cavitation equipment and a jet apparatus for erosion-corrosion. Cumulative mass loss vs. exposure time was used to evaluate the erosion rate of the two alloys. The surface and cross-sectional morphologies before and after the erosion tests were observed by scanning electron microscopy (SEM), the inclusions were analyzed by an energy dispersive spectroscopy (EDS), and the surface roughness was also measured by surface roughness tester to illustrate the evolution of erosion process. The results show that the cumulative mass loss of CE of Inconel 625 is about 1/6 that of Inconel 600 and the CE incubation period of the Inconel 625 is 4 times as long as that of the Inconel 600. The micro-morphology evolution of CE process illustrates that the twinning and hardness of the Inconel 625 plays a significant role in CE. In addition, the cumulative mass loss of JIE of Inconel 625 is about 2/3 that of Inconel 600 at impacting angle of 90 degrees, and almost equal to that of the Inconel 600 at impacting angle of 30 degrees. Overall, the resistance to CE and JIE of Inconel 625 is much superior to that of Inconel 600. (C) 2010 Elsevier By. All rights reserved.
关键词:
stress-corrosion cracking;aluminide intermetallic alloys;high-purity;water;mechanical-properties;crevice corrosion;solid particles;wear;behavior;microstructure;deformation;steam
Nuclear Engineering and Design
A composite coating was deposited on Inconel 600 substrate by cold spray method using pure Ni powder (60 wt.%) blended with alpha-Al(2)O(3) (40 wt.%) as feedstock. It is expected to be applied to repair the bellows eroded by the liquid droplet erosion (LDE). Microstructure of the coating was observed using optical microscope (OM) and scanning electron microscopy (SEM). Microhardness of the coating was determined by Vickers hardness tester. Cavitation erosion (CE) experiments were carried out in the distilled water. Jet impingement erosion (JIE) experiments were performed in slurry containing 1 wt.% quartz particle with the flow velocity of 15 m/s at impingement angles of 30 degrees, 60 degrees and 90 degrees, respectively. Cumulative mass loss vs. testing time was used to evaluate the erosion rate of the coating. The erosion mechanism was analyzed by OM, SEM, X-ray diffraction (XRD) and the microhardness measurement. The results show that the composite coating has compact microstructure and relatively high hardness. The resistance to CE of the coating is not as good as that of Inconel 600 substrate due to the weak bonds of the Al(2)O(3) particles. However, the results of the JIE test indicate that the slurry erosion resistance of the coating is better than that of Inconel 600 at the impact angles of 30 degrees and 60 degrees, but not at the normal impact angle. (C) 2011 Elsevier B.V. All rights reserved.
关键词:
large powder particles;composite coatings;slurry erosion;kinetic;spray;liquid impact;alloy;microstructure;steels;deposition;resistance