钢铁研究学报(英文版)
The effects of phase transformation on mechanical properties and pitting corrosion of 2205 duplex stainless steel have been investigated. The amount of σ phase in the test specimen was varied up to a maximum of 6% by thermal treatment at 850°C for period of time of up to 60 min. The results showed that σ phase both markedly increased the hardness and decreased the impact toughness of the test steel. But the increasing tendencies of the ultimate tensile strength and the yield strength were not obviously, while the total elongation abruptly decreased with the aging time from 5 min →15 min →60 min. SEM impact microfracturegraphs analysis revealed that the types of impact fracture changed from ductile mode to transcrystalline mode when the specimens aged from 5 min to 60 min. Furthermore, the extent of pitting potential reducing was found to be strongly temperature dependent, being more pronounced at the higher temperature. During the incubation period of σ phase nucleation, the pitting corrosion test temperature and the aging time had collaborative effects on evidently displacing the pitting potential towards less noble values. After 15 min, the higher temperature contributed more on decreasing the pitting potential than the aging time did.
关键词:
duplex stainless steel;phase transformation;mechanical properties;pitting corrosion
ZHANG Wei
,
YU Yan
,
FANG Yuan
,
LI Jian-guo
钢铁研究学报(英文版)
For many rapid or near-rapid solidification processes, the interfacial heat transfer between the melt and the substrate is a key issue on the cooling and solidification rate of castings. For the purpose of controlling and adjusting of the interfacial thermal resistance, the effects of C/BN, Zn and organic coatings on the instantaneous interfacial heat flux and the solidified structure of AISI304 stainless steel solidification on copper substrate have been investigated by using an experimental simulator. The results show that C/BN coatings can improve the uniformity of heat flux and solidified structure; Zn coating can increase the heat flux and solidification rate in the growth stage of the solidified shell; organic coating will decrease the heat flux and the solidification rate and make re-melted structure on the surface of the solidified shell.
关键词:
near rapid solidification
,
interfacial heat transfer
,
coating
Journal of Materials Research
The morphology of the dark and bright regions observed by transmission electron microscopy for the Zr(64.13)Cu(15.75)Ni(10.12)Al(10) bulk metallic glass strongly depends on the ion beam parameters used for ion milling. This indicates that the ion beam could introduce surface fluctuation to metallic glasses during ion milling.
关键词:
room-temperature
X.B. Tian
,
X.F. Wang
,
A.G. Liu
,
L.P. Wang
,
S. Y. Wang
,
B. Y. Tang and P. K. Chu 1)Advanced Welding Production & Technology National Key Laboratory
,
Harbin Institute of Technology
,
Harbin 150001
,
China 2)Department of Physics & Materials Science
,
City University of Hong Kong
,
China
金属学报(英文版)
The research on plasma immersion ion implantation has been conducted for a little over ten years. Much is needed to investigate including processing technlogy, plasma sheath dynamics, interaction of plasma and surface, etc. Of the processing methods elavated temperature technique is usually used in PIII to produce a thick modified layer by means of the thermal diffusion. Meanwhile plasma ion heating is more recently developed by Ronghua Wei et al[1]. Therefore the temeperature is a critical parameter in plasma ion processing. In this paper we present the theoretical model and analysize the effect of imlantation voltage, plasma density, ion mass,etc on the temperature rise.