ZHAO Cai
,
TANG Di
,
JIANG Haitao
,
ZHAO Songshan
,
LI Hui
钢铁研究学报(英文版)
The quenching and partitioning (Q&P) process was experimentally investigated on the thermomechanical simulator (Gleeble3800). The microstructure and fracture mechanism of the sheets were investigated by means of TEM. It was found that the microstructure of quenched and partitioned steel consists of fine lath martensite and thin interlath austenite films. The optimum quenching temperature of producing the maximum amount of retained austenite after final quenching at room temperature was predicted by Matlab software package. It was found that the calculations by Matlab software can provide guidance for experimental processing design reliably. The volume fraction of retained austenite at room temperature was approximately 8%, which was measured easily by the software VC60++ programming. The results verified that quenched and partitioned steel possesses a good combination of strength and plasticity due to its fine microstructure. This steel exhibited high ultimate tensile strength (exceeding 1 000 MPa) and good elongation of 25%. The results showed that the fracture mechanism of the sheets is typical tough fracture under the condition of tensile failure.
关键词:
Q&P;Matlab software;microstructure;mechanical property
张宝艳
,
陈祥宝
,
李敏
,
邢丽英
,
汪亮
,
蒋诗才
航空材料学报
doi:10.3969/j.issn.1005-5053.2002.01.008
探讨了树脂基体、碳纤维增强体以及树脂基体-纤维的界面等对双马来酰亚胺(简称双马)树脂基复合材料冲击后压缩强度(CAI)值的影响,指出降低树脂基体的交联密度和产生微观两相结构是提高碳纤维/双马复合材料CAI值的两个典型方法.合适的树脂含量有利于保持复合材料体系较高的CAI值,采用高强高韧性的碳纤维可明显提高复合材料体系的CAI值.为获得较高的CAI值,保持合适的树脂基体-纤维界面性能也是必要的.
关键词:
双马来酰亚胺
,
纤维增强复合材料
,
韧性
,
界面
中国腐蚀与防护学报
N。1Atmospheric Corrosivlty for Steels………………………………………………… .LIANG Caideng HO[I i。-tat（6）Caustic Stress Corrosion Cr。king of Alloy 800 Part 2.The Effect of Thiosul执e……………………………………… KONG De-sheng YANG Wu ZHAO Guo-zheng HUANG De.ltL。ZHANG Yu。。he CHEN She。g-bac（13）SERS slid E16CttOCh6iniC81 Stlldy Of Illhibit1Oli M6ch＆tllsth Of ThlollY68 Oil ITOll ID H....
关键词:
Europhysics Letters
Noncollinear magnetic investigations of the ground state in PrFeAsO have been performed by the density-functional theory. We calculated the total energy and made structure optimization, and the electronic density of states of PrFeAsO was analyzed. There are three different magnetic structures in PrFeAsO defined by experiments. Based on these magnetic structures, we studied four collinear and four noncollinear cases. The ground state is found to take the ordering proposed by Zhao, in which the FeAs plane is of stripe antiferromagnetism and Pr spins are perpendicular to Fe spins. The electronic density of states indicates that for PrFeAsO the increase of the electron Coulomb interaction leads to a decrease in conductivity. Copyright (C) EPLA, 2011
关键词:
high-temperature superconductivity;phase-diagram;oxypnictides;instability
段友社
,
郭书良
,
吴刚
,
侯军生
复合材料学报
基于热压罐成型工艺,选择了树脂柱Z向增强泡沫芯材、碳纤维Z向增强泡沫芯材、Kevlar纤维缝纫增强泡沫芯材3种Z向增强复合材料结构,对夹芯结构进行了低速冲击损伤和冲击后压缩（CAI）性能研究,考察了不同Z向增强方式对冲击损伤面积和破坏模式的影响。结果表明,Z向增强对泡沫芯材产生了初始损伤,其冲击后损伤面积大于未增强泡沫夹芯结构;但Z向增强改变了夹芯结构的压缩破坏机制。通过选用合适的Z向增强材料和Z向增强参数,能够提高夹芯结构的压缩强度和CAI强度。其中当增强材料为碳纤维,增强参数为10mm×10mm时,压缩强度提高了13%,CAI强度提高超过40%。
关键词:
复合材料
,
泡沫夹芯
,
Z向增强
,
冲击损伤
,
冲击后压缩
张子龙
,
程小全
,
益小苏
复合材料学报
doi:10.3321/j.issn:1000-3851.2002.05.021
为了考察一种小试件CAI试验方法的有效性,本文作者对复合材料层合板的准静态横向压缩特性和损伤,以及损伤后的压缩破坏进行了试验研究,采用C扫描、热揭层等技术对层合板内的损伤进行测量,并将含准静态横压损伤层合板的剩余压缩强度与低速冲击后板的压缩强度进行了比较.结果表明:在横压过程中存在分层损伤起始门槛压缩载荷值或压入深度值,以及横压载荷极限值;小板试件各界面的分层面积沿厚度方向的分布和继后的压缩破坏形式等与SACMA的CAI试验标准的情况相异.
关键词:
复合材料层合板
,
低速冲击
,
准静态横向压缩
,
损伤
,
压缩破坏
王浩
,
郑亚萍
,
张娇霞
,
许亚洪
,
戴峰
宇航材料工艺
doi:10.3969/j.issn.1007-2330.2009.04.014
针对氰酸酯采用环氧树脂进行改性研究,对该体系的流变性能与DMA进行分析,并对浇注体的力学性能进行了研究.以聚砜作为增韧剂,采用"离位"增韧技术,制备复合材料层压板,测试了复合材料的力学性能与冲击后压缩强度(CAI),对微观增韧机理进行了研究.结果表明,在40℃时,氰酸酯/环氧树脂体系有较长的工艺适用期,很好的工艺操作性.Tg为200℃时,浇注体的力学性能优良.采用热塑性树脂作为"离位"增韧层,体系出现了相反转结构,具有较好的增韧效果,复合材料的CAI值从180 MPa增加到260 MPa,对复合材料的力学性能没有影响.
关键词:
氰酸酯
,
"离位"增韧改性
,
冲击后压缩强度
刘建国
,
安振涛
,
张倩
,
杜仕国
,
姚凯
,
王金
材料导报
doi:10.11896/j.issn.1005-023X.2017.04.030
为评估氧化剂硝酸羟胺的热稳定性,使用标准液体铝皿于3 K/min、4 K/min、5 K/min加热速率下进行热分析.借助非等温DSC曲线的参数值,应用Kissinger法和Ozawa法求得热分解反应的表观活化能和指前因子,根据Zhang-Hu-Xie-Li公式、Hu-Yang-Liang-Xie公式、Hu-Zhao-Gao公式以及Zhao-Hu-Gao公式,计算硝酸羟胺的自加速分解温度和热爆炸临界温度,并对热分解机理函数进行了研究.设计了7条热分解反应路径,采用密度泛函理论B3LYP/6-311++G(d,p)方法对硝酸羟胺的热分解进行了动力学和热力学计算.计算结果表明,硝酸羟胺热分解的自加速分解温度TsADT=370.05 K,热爆炸临界温度Te0=388.68K,Tbp0=397.54 K,热分解最可几机理函数的微分形式为f(a) =17×(1-α)18/17.硝酸羟胺热分解各路径中,动力学优先支持路径Path 6、Path 5、Path 4和Path 1生成NO和NO2,其次是Path 2、Path 7和Path 3生成N2和N2O.温度在373 K以下时,Path 1'反应无法自发进行,硝酸羟胺无法进行自发的热分解.从热力学的角度来看,硝酸羟胺在370.05K以下储存是安全的.
关键词:
硝酸羟胺
,
热分析
,
热稳定性
,
热分解机理
,
密度泛函理论
中国有色金属学报(英文版)
doi:10.1016/S1003-6326(16)64373-X
提出了一种从氧化铝中提取原铝的新方法。该方法的原理基于如下化学反应：AlI3+(3/2)Zn=Al+(3/2)ZnI2。首先通过氧化铝的碳热氯化反应得到氯化铝(AlCl3)，然后通过氯化铝和碘化钙的交换反应(AlCl3+CaI2→AlI3+CaCl2)得到碘化铝。在实验室条件下对这些反应进行了研究，同时对一些回收主要化学试剂的反应进行了研究(Cl2, ZnI2→Zn, CaCl2→CaI2)。采用XRD和SEM对反应产物的相组成及形貌进行分析。采用总自由能最小方法对化学反应平衡进行计算。结果表明，采用非电解方法，可以在没有非常高的温度和可消耗的化学试剂的条件下，从氧化铝中有效地提取铝。与当今采用燃煤发电提供电力的铝电解厂相比，本方法所产生的单位碳消耗和 CO2大气排放可以降低一半以上。
关键词:
铝
,
铝合金
,
氯化物
,
碘化物
,
锌
,
碘
,
高速冶金
益小苏
,
许亚洪
,
唐邦铭
,
陈永刚
,
张子龙
材料工程
doi:10.3969/j.issn.1001-4381.2004.09.001
复合材料的结构一体化技术包括结构整体化和结构-功能一体化两个方面.复合材料吸能结构属于典型的结构-功能一体化结构.以复合材料管形件为基础,发现提高管形件轴向性能如增加编织结构的轴向纤维纱数,或调整预浸料复合材料铺层尽可能地平行于轴向,或提高复合材料层间韧性(即高CAI值)等,都有利于提高吸能效果.在整体化制造方面,研制和验证了织物复合材料正弦波梁的液态成型制造技术.
关键词:
复合材料
,
吸能行为
,
正弦波梁
,
液态成型
,
编织结构