THE FAILURE MECHANISM OF REVERSE SHAPE MEMORY EFFECT IN A Cu-BASE ALLOY

C.M Li , G.X. Dong , S.T- Dai , and D. Y Chen (Tsinghua University Beijing 100084 , China)J Yin and D.X. Hu (Shanghai No.5 Steel Works , Shanghai 200940 , China)

金属学报(英文版)

The interior structural evolution accompanying reverse shape memory effect (RSMEin a Cu-Zn-Al alloy was studied by means of transmission electron microscopy. It was found that RSME is closely related to bainitic transformation in this alloy during the isothermal reaction at moderate temperatures. At a given temperature and a certain external constraint stress, the shape memory effect depends mainly on the aging time.During the early stage, the shape memory effect enhances with the increase of reactiotn time. Then it will decrease gradually apon further aging. If the alloy is overaged, the stacking faults of bainite will disappear gradually by the motion of partial dislocations through which long range diffusion of solute atoms takes place, giving rise to the deterioration of RSME. When all the bainite transforms to α phase, RSME will lose completely.

关键词: reverse shape memory effect , null , null , null

University of Science and Technology Beijing

JIA Shizhen University of Science and Technology Beijing , China.

材料科学技术（英文）

关键词:

RF deflecting cavity design for bunch length measurement of photoinjector at Tsinghua University

中国物理C

关键词:

Design of an MeV ultra-fast electron diffraction experiment at Tsinghua university

中国物理C

关键词:

Abstracts of papers from Journal of University of Science and Technology Beijing

稀有金属（英文版）

关键词:

CORRELATION BETWEEN STRESS COMPONENTS AND STRESS CORROSION CRACKS IN BRASS Lecturer,Department of Materials Physics,University of Science and Technology Beijing,Beijing 100083,China

QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing , Beijing , China

金属学报(英文版)

The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.

关键词: stress corrosion cracking , null , null , null

TW Laser system for Thomson scattering X-ray light source at Tsinghua University

中国物理C

关键词:

Generating 10-40 MeV high quality monoenergetic electron beams using a 5 TW 60 fs laser at Tsinghua University

HUA Jian-Fei , YAN Li-Xin , PAI Chih-Hao , ZHANG Chao-Jie , LI Fei , WAN Yang , WU Yi-Peng

中国物理C doi:10.1088/1674-1137/39/1/017001

关键词:

Ion sputter erosion in metallic glass-A response to "Comment on: Homogeneity of Zr(64.13)Cu(15.75)Ni(10.12)Al(10) bulk metallic glass" by L-Y. Chen, Y-W. Zeng, Q-P. Cao, B-J. Park, Y-M. Chen, K. Hono, U. Vainio, Z-L. Zhang, U. Kaiser, X-D. Wang, and J-Z Jiang J. Mater. Res. 24, 3116 (2009)

Journal of Materials Research

The morphology of the dark and bright regions observed by transmission electron microscopy for the Zr(64.13)Cu(15.75)Ni(10.12)Al(10) bulk metallic glass strongly depends on the ion beam parameters used for ion milling. This indicates that the ion beam could introduce surface fluctuation to metallic glasses during ion milling.

关键词: room-temperature

Chen系统的状态变量周期性反馈控制

李开明 , 李亚洲 , 冯维贵 , 林长

量子电子学报 doi:10.3969/j.issn.1007-5461.2007.05.014

采用非线性反馈控制,用附加了带参数的正弦项对Chen系统进行了有效的控制.随着参数k的逐渐增大,系统的动力学行为呈现出一系列的变化.数值研究结果表明:随控制参数的增大,驱动信号的强度渐大,混沌系统由混沌运动到周期轨道,最终到一相点.

关键词: 混沌 , Chen系统 , 不动点 , Lyapunov指数 , 反馈控制