XING Zhanping*
,
GUO Jianting
,
HU Zhuangqi
,
AN Geying*Institute of Metal Research
,
Chinese Academy of Sciences
,
Shenyang
,
China * Harbin Institute of Technology
,
Harbin
,
China
金属学报(英文版)
Ni-50at.%A1 matrix composites containing 0 to 20v.% TiB2 particles have been successfully fabricated by HPES technique. The results show that the Vickers hardness at room temperature and the compressive yield strength from room temperature to 1000℃ of the composites increase with increasing volume fraction of the strengthening phase. Especially, the yield strength of NiAl-20TiB2 was approximately twice as high as that of unreinforced NiAl. The ductility of the composites at room temperature is also superior to the monolithic NiAl.
关键词:
intermetallic matrix composite
,