Yuping ZENG
,
Dongliang JIANG
,
Shouhong TAN and Jingkun GUO(Shanghai Institute of Ceramics
,
Chinese Academy of Sciences
,
Shanghai 200050
,
China)
材料科学技术（英文）
Ceramic tapes, containing Al2O3-25 wt pct TiB2(B) and Al2O3-25 wt pct nano-TiC (c), have been obtained by tape casting process. Numerous tapes (about 60～80 tapes) were prepared by stacking in turn the composition (B) and (C), laminating under 10 MPa pressure, eliminating the solvent and burning out the polymer additives. The final green bodies were hot pressed at 1750℃ and 30 MPa. The composite has a bending strength of 568 MPa and a fracture toughness of 5.8 M Pa·m1/2. SEM analysis exhibits that Al2O3 particle growth was inhibited by TiC particles in C. but TiB2 particles could not hinder Al2O3 growth in B. The curves of GTA indicates that all organic additives could be removed completely above 600℃
关键词:
Xinwen ZHU
,
Dongliang JIANG
,
Shouhong TAN
材料科学技术（英文）
An innovative approach has been developed to fabricate reticulated porous ceramics (RPCs) with uniform macrostructure by using the polymeric sponge as the templates. In this approach, the coating process comprises of two stages. In the first stage, the thicker slurry was used to coat uniformly the sponge substrate. The green body was preheated to produce a reticulated perform with enough handling strength after the sponge was burned out. In the second stage, the thinner slurry was used to coat uniformly the preform. The population of the microscopic and macroscopic flaws in the structure is reduced significantly by recoating process. A few filled cells and cell faces occur in the fabrication and the struts were thickened. A statistical evaluation by means of Weibull statistics was carried out on the bend strength data of RPCs, which were prepared by the traditional approach and innovative approach, respectively. The result shows that the mechanical reliability of RPCs is improved by the innovative approach. This innovative approach is very simple and controlled easily, and will open up new technological applications for RPCs.
关键词:
Reticulated porous ceramics
,
null
,
null
,
null
,
null