THE EFFECT OF BORON AND CARBON ADDITION ON WELDABILITY OF DS TMS-75 SUPERALLOY

M.C.Chaturvedi , Y.L.Wang , N.L.Richards

金属学报(英文版)

Four alloys TMS-75 (Base), Base+B, Base+C and TMD-103 (Base+B+C) with varying levels of B, C were directionally solidified (DS), and their weldability was investigated by bead-onplate electron beam welding. It was found that cracking occurred in the weld-metal, as well as in the heat affected zone (HAZ). Both γ/γ' and/or γ/carbide eutectic contributed to the weld-metal cracking, and theγ/γ' eutectic was found to be mainly responsible for cracking in HAZ. However, constitutional liquation of carbides seems to have made some contribution also.The B addition had a detrimental effect on HAZ cracking susceptibility, while C addition improved it appreciably even in the presence of B. In addition, no obvious differences were observed in cracking susceptibility of weld-metal in the four alloys. The cracking modes and mechanisms underlying the effect of B and C addition on weidability could be explained on the basis of microstructures of the four alloys.

关键词: Ni-based superalloy , null , null

出版年份

刊物分类

相关作者

相关热词