Shenhua SONG
,
R.G.Faulkner
,
P.E.J. Flewitt
,
Dongdong SHEN
,
Jing LIU
,
Zexi YUAN
材料科学技术（英文）
Irradiation-induced impurity segregation to grain boundaries is one of the important radiation effects on materials. For this reason, phosphorus segregation to prior austenite grain boundaries in a P-doped 2.25Cr1Mo steel subjected to neutron irradiation is examined using field emission gun scanning transmission electron microscopy (FEGSTEM) with energy dispersive X-ray microanalysis (EDX). The steel samples are irradiated around 270 and 400℃, respectively. The irradiation dose rate and dose are ～1.05×10-8 dpa/s and ～0.042 dpa respectively for 270℃ irradiation, and 1.7×10－8 dpa/s and 0.13 dpa respectively for 400℃ irradiation. The FEGSTEM results indicate that there is no apparent phosphorus segregation during 270℃ irradiation but there is some during 400℃ irradiation
关键词:
Neutron irradiation
,
null
,
null
,
null
S.H.Song
,
Z.X.Yuan
,
J.Liu
,
R.G.Faulkner
金属学报(英文版)
Irradiation-induced grain boundary segregation of solute atoms frequently bring about grain boundary precipitation of a second phase because of its making the solubility limit of the solute surpassed at grain boundaries. Until now the kinetic models for irradiation-induced grain boundary precipitation have been sparse. For this reason, we have theoretically treated grain boundary precipitation under irradiation in dilute binary alloys. Predictions of γ'-Ni3 Si precipitation at grain boundaries are made for a dilute Ni-Si alloy subjected to irradiation. It is demonstrated that grain boundary silicon segregation under irradiation may lead to grain boundary γ'-Ni3Si precipitation over a certain temperature range.
关键词:
segregation
,
null
,
null