THE PROPERTIES OF SILICA FUME MAGNESIUM OXYCHLORIDE CEMENT MATERIALS

H.F.Yu 1) , P.Q.Liu 1) and W.H.Wang 2) 1) Department of Materials Science and Engineering , Shenyang Architectural and Civil Engineering Institute , Shenyang 110015 , China 2) Department of Airport , CAAC Eastnorth Management , Shenyang 110043 , China

金属学报(英文版)

The properties of a new magnesium Oxychloride cement (MOC) material formed by silica fume uniformly mix in MOC paste was presents. The influence of silica fume on the water resistance and compressive strength of MOC paste was invesigated in this study. It is shown that when 30 weight percent of silica fume is added to the MOC paste, a high strength and water resisting new material with 112MPa compressive strength and 1 00 water resisting coefficient could by obtained.

关键词: silica fume , null , null , null

RESEARCH ON THE RHEOLOGY OF MAGNESIUM OXYCHLORIDE CEMENT Ⅱ—STUDY OF INFLUENTI AL FACTORS ON RHEOLOGICAL PROPERTIES

H.F.Yu and P.Q.Liu Department of Materials Science and Engineering , Shenyang Architectural and Civil Engineering Institute , Shenyang 110015 , China

金属学报(英文版)

The influences of solution cement ratio (Wn/C), MgO content of the magnesia, specific gravity of the MgCl 2 solutions and mixing regime on the rheological properties of magnesium oxychloride cement (MOC) pastes were studied with a rotating viscometer. It was found that different influential factors cause difference rheological properties of the MOC pastes.

关键词: magnesium oxychloride cement (MOC) , null , null