Directional solidification experiments were carried out for succinonitrile-1.0 wt pct acetone alloy with the orientation of dendritic arrays being not parallel to the direction of the temperature gradient. Experimental results show that there exists an allowable range of primary dendritic spacing under a given growth condition. The average primary spacing depends not only on the current growth conditions but also on the way by which the conditions were achieved. The upper limit of the allowable range becomes smaller in comparison with that with <001> direction of dendrite arrays parallel to the direction of the temperature gradient, which means that the history-dependence of dendritic growth is weaker under this condition. The lower limit obtained is compared with a self-consistent model, which shows a good agreement with experimental results.
关键词:
Directional solidification
,
枝晶一次间距
,
历史相关性
Guanghui MENG
,
Xin LIN
,
Weidong HUANG
材料科学技术（英文）
Based on the Jackson and Hunt’s analysis, the selection of lamellar spacing in regular eutectics was reexamined at low velocity. The isothermal assumption was released and the effective interface undercooling was determined by the weighted average of the eutectic phases. It is found that the lamellar spacing minimized the effective interface undercooling depends only on the intrinsic characteristics of a given system at a fixed velocity. In addition, the selection of lamellar spacing is related to the relationship between the average interfacial undercoolings of the eutectic phases and the lamellar spacing. The selected lamellar spacing obviously deviated from that predicted by the Jackson and Hunt’s analysis if the variation of the average interfacial undercoolings of the solid phases with the lamellar spacing was markedly different at a constant growth rate.
关键词:
Solidification
,
null
,
null
,
null