L.M. Liu (National Key Laboratory of Advanced welding Production Technology
,
HIT
,
Harbin 150001
,
China)
金属学报(英文版)
Tensile strength of diffusion welded joint of aluminum matrix composite is very low due to its poor weld- ability.In this paper, solution and age treatments were conducted on the welded joint of Al2O3p/ 6061Al composite subjected to diffusion welding using Gleeble 1500 machine, and ensile strength and microstructure of welded joint aged at175℃ were measured and analyzed respectively, Results showed that aging precipitation of welded joint is promoted effectively because of redistribution of reinforcement and a few number of dislocations in the matrix of weld zone resulting from welding pressure,and hence tensile strength of welded joint is increased significantly after aging treatment.