金属学报(英文版)
The variation of cyclic stress,internal friction and ultrasonic attenuation during cyclic deformation and relations among them have been investigated with different slip orientation Al single crystals.The results indicate that the value of cyclic stress σ,internal friction Q~(-1)and ultrasonic attenuation △α depend obviously on the slip orientation.There are large differences in above three parameters for different slip orientation Al crystals.In early stage of fatigue life,σ and △α increase and Q~(-1)decreases with cycles N,and △α reached maxi- mum before σ,while Q~(-1)and σ get the valley and the peak,respectively,at same cycles.
关键词:
crystal orientation
,