A secondary twinning orientation relationship between A and B martensite variants in a CuZnAl shape memory alloy was confirmed under TEM observation.The twin plane, (50),is a linear combination of (8)and(1 0 10)planes,which are twin planes of A:C and A:D type pair respectively.
关键词:
shape memory alloy
,
null
,
null
,
null
LIU Junming LIU Zhiguo WU Zhuangchun Nanjing University
,
China LIU Junming
,
lecturer
,
National Laboratory of Solid State Microstructuros
,
Nanjing University
,
Nanjing 210008
,
China
金属学报(英文版)
The profile features of the solidifying interface of the irregular Al-Si eutectic during directional solidification are studied by numerically solving a nonlinear coupling equation of directional solidification of this eutectic.The critical splitting point of the solidifying interface coincides with the maximum value of its position and corresponds to the marginal stability point.Argument is presented that the interlamellar spacing for local regular structure selects the critical splitting state of the α(Al)-liquid interface as its operating point,and the oper- ating point of the average interflake spacing for the irregular structure is the critical splitting state of the β(Si)-liquid interface.The scaling laws derived,which have the more general forms than the classic Jackson-Hunt scaling,gained support from the experimental results.
关键词:
irregular Al-Si eutectic
,
null
,
null
Junming LIU Zhiguo LIU Zhuangchun WU National Lab.of Solid State Microstructures
,
Nanjing University
,
Nanjing 210008
,
China
材料科学技术（英文）
As a simulation of surface solidification of materials,quasi-two dimensional dendritic deposition of ammonium chloride(NH_4Cl)crystals from an aqueous solution film with free surface by vapourization was investigated by the in- situ observation technique.The depositing morphologies of NH_4Cl crystals are faceted and of growth laws differing from the three-dimensional case.Under low supersaturation,faceted dendrites formed,whereas the anisotropy in growth kinetics decreases with the increase of supersaturation.When vapourizing rate(supersaturation)is not very low, oscillations of growth rate.tip-radius and second arm spacing of the dendrites were observed.It is suggested that this dynamic phenomenon is attributed to the correlation between the convection-transfer effect induced by the surface tension gradient of solution film.and the driving force for deposition.
关键词:
surface deposition
,
null
,
null
,
null