LIU Changhui
,
HE Huahui
,
SHEN Xiang
,
LI Haihua
钢铁研究学报(英文版)
Electroless CoFeB films with good soft magnetic properties were fabricated on polyester plastic substrate from sodium tartarate as a complexing agent. The plating rate of electroless CoFeB films is a function of concentration of sodium tetrahydroborate, pH of the plating bath, plating temperature and the metallic ratio. The estimated regression coefficient b0-b3 confidence interval, residual error r and confidence interval rint were confirmed by a computer program. The optimal composition of the plating bath was obtained and the dynamic electromagnetic parameters of films were measured in the 2-10 GHz range. At 2 GHz, the μ′, μ″ of the electroless CoFeB films were 304 and 766, respectively, as the concentration of reducer is 1 g/L. Magnetic hysteresis loop of the deposited CoFeB films show a remanence close to the saturation magnetization and coercivity of about 557-1274 A/m. The loops along the hard axis display low anisotropic field Hk of 2 388-3 582 A/m.
关键词:
electroless CoFeB deposits;deposition rate;multiple linear regression;coercivity;magnetic hysteresis loop