Sugui TIAN
,
Jinghua ZHANG
,
Yongbo XU
,
Zhuangqi HU
,
Hongcai YANG
材料科学技术（英文）
The microstructures of a single crystal Ni-base superalloy with [001] orientation were observed by means of TEM. Results showed that the fine gamma' particles were precipitated in the gamma matrix channels during the tensile deformation of the alloy. Thermodynamics analysis indicated that the solubility of elements M(Al,Ta) within the gamma matrix may be changed when the alloy was deformed by the external applied stress. The tensile stress reduced the solubility of elements Al and Ta so as to occur the over-saturation and agglomeration of them, which promoted the precipitation of fine gamma'-phase in the gamma matrix.