Effect of Tempering Temperature on Microstructure and Properties of E690 Offshore Plate Steel

ZHANG Jie , CAI Qing-wu , WU Hui-bin , ZHANG Kun , WU Bo

钢铁研究学报(英文版)

A new kind of Mn-Mo-Nb-Cu-B bainite steel which satisfied mechanical demands of E690 offshore plate steel was designed. The effect of two processes——thermomechanical control process (TMCP)+tempering (T) and thermomechanical control process (TMCP)+reheating and quenching (RQ)+tempering (T)——on micros...

关键词: offshore plate , low carbon bainitic steel , tempering , toughness , EBSD

Effect of Nb to Austenite Recrystallization in High Temperature Deformation Processing

JIAO Duo-tian , CAI Qing-wu , WU Hui-bin , et al

钢铁研究学报(英文版)

By analysing the stepped test pieces with optical microscope, the influence of the Technological parameters including rolling temperature and reduction amount on the Austenitic recrystallization fraction of Nb content of 0.08％ steel deformed in high temperature processing was studied, and the deform...

关键词: Austenicic Recrystallization;Technological Parameter;high content Nb

Effect of Heat Treatment Process on Properties of 1000 MPa Ultra-High Strength Steel

YU Wei , QIAN Ya-jun , WU Hui-bin , YANG Yue-hui

钢铁研究学报(英文版)

Two types of steel, C-Mn-Cr-Mo-B microalloyed steel and C-Mn-Mo-Nb-Cu-B microalloyed steel, are designed to develop 1000 MPa ultra-high strength steel. Two kinds of processes, thermomechanical controlled process (TMCP) combined with traditional off-line quenching and tempering (QT) process versus co...

关键词: Heat treatment, High strength steel, Microtructures, Mechanical properties

Effect of Heating Rate Before Tempering on Reversed Austenite in Fe-9Ni-C Alloy

ZHANG Kun , TANG Di , WU Hui-bin

钢铁研究学报(英文版)

The alloy was reheated to 580 ℃ for tempering at rates of 2, 5, 10, 20, and 40 ℃/s, respectively, after quenching. The amount, distribution, and stability of reversed austenite were investigated by X-ray diffraction (XRD) and electron back scatter diffraction (EBSD). The microstructure and cryogenic...

关键词: 9Ni steel , heating rate , reversed austenite , cryogenic toughness

High Temperature Deformation Behavior of Fe-9Ni-C Alloy

ZHANG Kun , WU Hui-bin , TANG Di

钢铁研究学报(英文版)

The high temperature deformation behavior of the 9Ni steel has been studied by the Gleeble-3500 tester. The relationship between deformation resistance and deformation degree, deformation temperature and deformation rate was revealed. The results show that when the deformation degree is less than 0...

关键词: 9Ni steel , high temperature deformation resistance , mathematical model