金属学报(英文版)
A tubular micro filtration membrane was prepared with α alumina powder and ceramic tube support using dip coating method. The prepared membrane was characterized by SEM, mercury porosimetry and permeability measurement. The effects of the suspension properties and the preparation conditions on the structure and the membrane properties were discussed. The membrane was made with a top layer thickness of 50 μm , an average pore diameter of 0 45 μm , a porosity of 42% and a water flux of 6 5×10 -2 l/(m 2 h Pa). The membrane has a narrow pore distribution and good strength without crack forming, which can be used in industrial micro filtration process.
关键词:
ceramic membrane
,
null
,
null
,
null
Y.S. Sun
,
W.M. Zhang
,
X.G. Min
金属学报(英文版)
Small amount of calcium addition to the Mg-9Al-0. 8Zn-0.2Mn(AZ91) alloy resulted in the obvious influence on mechanical properties. The yield strength of the alloys increased with the increase of Ca addition and maximum strength was obtained from the alloy containing 0.15% of Ca. The creep resistance at the temperatures between 150-200°C was also significantly increased with Ca addition. The creep rate (at 200°C,50MPa) of the alloy with 0. 15% of Ca addition was one order of magnitude lower than that of the base alloy (AZ91). Microstructural observations revealed that the addition of calcium refined the microstructure and enhanced the thermal stability of the β precipitates, which accounted for the improvement of creep resistance at high temperatures.
关键词:
tensile strength magnesium alloy
,