Y.X. Chen L.H. He P.J. Shang Q.L. Tang Z.Q. Liu H.B. Liu L.P. Zhou
材料科学技术（英文）
Micro-sized (1030.3§178.4 nm) and nano-sized (50.4±8.0 nm) Fe3O4 particles have been fabricated through hydrogen thermal reduction of α-Fe2O3 particles synthesized by means of a hydrothermal process. The morphology and microstructure of the micro-sized and the nano-sized Fe3O4 particles were characterized by X-ray diffraction, field-emission gun scanning electron microscopy, transmission electron microscopy and high-resolution electron microscopy. The micro-sized Fe3O4 particles exhibit porous structure, while the nano-sized Fe3O4 particles are solid structure. Their electrochemical performance was also evaluated. The nano-sized solid Fe3O4 particles exhibit gradual capacity fading with initial discharge capacity of 1083.1 mAhg¡1 and reversible capacity retention of 32.6% over 50 cycles. Interestingly, the micro-sized porous Fe3O4 particles display very stable capacity-cycling behavior, with initial discharge capacity of 887.5 mAhg¡1 and charge capacity of 684.4 mAhg−1 at the 50th cycle. Therefore, 77.1% of the reversible capacity can be maintained over 50 cycles. The micro-sized porous Fe3O4 particles with facile synthesis, good cycling performance and high capacity retention are promising candidate as anode materials for high energy-density lithium-ion batteries.
关键词:
Lithium-ion battery
,
null
,
null
Y.X. Chen L.H. He P.J. Shang Q.L. Tang Z.Q. Liu H.B. Liu L.P. Zhou
材料科学技术（英文）
Micro-sized (1030.3§178.4 nm) and nano-sized (50.4±8.0 nm) Fe3O4 particles have been fabricated through hydrogen thermal reduction of α-Fe2O3 particles synthesized by means of a hydrothermal process. The morphology and microstructure of the micro-sized and the nano-sized Fe3O4 particles were characterized by X-ray diffraction, field-emission gun scanning electron microscopy, transmission electron microscopy and high-resolution electron microscopy. The micro-sized Fe3O4 particles exhibit porous structure, while the nano-sized Fe3O4 particles are solid structure. Their electrochemical performance was also evaluated. The nano-sized solid Fe3O4 particles exhibit gradual capacity fading with initial discharge capacity of 1083.1 mAhg¡1 and reversible capacity retention of 32.6% over 50 cycles. Interestingly, the micro-sized porous Fe3O4 particles display very stable capacity-cycling behavior, with initial discharge capacity of 887.5 mAhg¡1 and charge capacity of 684.4 mAhg−1 at the 50th cycle. Therefore, 77.1% of the reversible capacity can be maintained over 50 cycles. The micro-sized porous Fe3O4 particles with facile synthesis, good cycling performance and high capacity retention are promising candidate as anode materials for high energy-density lithium-ion batteries.
关键词:
Lithium-ion battery
,
null
,
null