Zhibin HUANG
金属学报(英文版)
Platinum films were sputter-deposited on two groups of nickel alloy substrates, in which the first group was the samples with rough surface, and the other group with polished surface. The platinum thin-films were applied to serve as the low-emissivity layers to reflect thermal radiation. Then, the platinum-coated samples were heated in air at 600 ℃ for 200~h to explore the effect of high-temperature environment on the emissivity of coated platinum film. After annealing, the average IR emissivity (at the wavelength of 3-14 μm) of the platinum film was only about 0.1 for polished sample and 0.45 for rough sample. The diffusion between platinum and the nickel-alloy elements at
600 ℃ had been also discussed.
关键词:
Low-emissivity layer
,
Platinum film
,
Infrared emissivity