金属学报(英文版)
Mechanically alloyed NiAl-TiB_2-Y_2O_3 composite (volume percentage of dispersoids about 15v%) was prepared by hot pressing. The compressive properties of the composite from 300 K to 1360 K were tested and the microstructures were studied mainly by TEM. The yield strengths of the composite at room temperature and high temperatures are considerably higher than that of monolithic NiAl and also is higher than similar NiAl-based composites which contained higher content of dispersoids but showed coarser microstructure. The possible strengthening mechanisms working in the composite are discussed.
关键词: : NiAl , null , null
程天一
材料研究学报
高熔点(1638℃)既是NiAl的优点也是其研制的障碍之一.本文报导用热压反应烧结法制备单相NiAl和(NiAl+Ni3Al)两相金属间化合物及其室温微观组织结构和压缩力学性能.
关键词: NiAl , hot pressure reaction sintering