Effect of different cooling history on yield ratio of HP295 steel for welded gas cylinder was studied and the result implied that both fine microstructure and good mechanical properties can be attained by using two-stage cooling and controlling the coiling temperature. The yield ratio of HP295 steel sheet was reduced to less than 0.8 by two-stage cooling process. The pass percent of yield ratio was enhanced from less than 90% to 100%. The mechanical properties satisfied the criteria of GB6653-1994.
关键词:
HP295 steel sheet
,
屈强比
,
两段式冷却
,
卷取温度
陈兴福
,
杨同利
,
肖继明
,
朱宁
,
何晓峰
,
邹秋兰
钢铁钒钛
介绍了某钢铁公司热连轧厂生产的HP295在用户加工使用过程中产生开裂的问题,针对这一问题,通过对力学性能和显微组织的分析,对化学成分及轧制工艺进行了优化,降低C、Mn及P含量,减少带钢的各向异性,同时采用终轧温度850～890℃,两段式冷却,卷取温度630～670℃,并根据季节变化适当微调的工艺,获得了较高比例的和细小均匀的铁素体以及弥散分布的珠光体组织,且屈强比也较低,使平均开裂率从约1％降低到0.3％.
关键词:
HP295
,
开裂
,
各向异性
,
两段式冷却
,
屈强比
朱伏先
,
佘广夫
,
张中平
,
李鑫
,
刘相华
钢铁
为探讨工业生产条件下降低铁素体/珠光体钢屈强比的有效办法,研究了前段冷却、后段冷却和两段式冷却3种工艺对HP295焊瓶钢板屈强比的影响规律,通过采用两段冷却方式并控制带钢卷取温度使攀钢HP295焊瓶钢板的屈强比低于0.8,屈强比合格率由此前的不足90%提高到100%,各项力学性能满足国家标准GB6653-1994要求.
关键词:
HP295焊瓶钢
,
屈强比
,
两段式冷却
,
卷取温度