Semi-solid slurry of A356 alloy was prepared by low superheat pouring and slightly electromagnetic stirring, and the fractal characteristics of morphology in semi-solid primary phase was researched. The fractal dimensions of primary phase morphology in the semi-solid A356 alloy were calculated by the program written to calculate the fractal dimensions of box-counting in the image of solid phase morphology in semi-solid metal slurry. The results indicated that the morphology of primary phase in semi-solid A356 prepared by low superheat pouring and slightly electromagnetic stirring is characterized by fractal dimension, and the primary phase morphology obtained by the different processing parameters has different fractal dimensions. The morphology of primary phase at the different position of ingot has different fractal dimensions, which reflected the effect of solidified conditions at different positions in the same ingot on the morphology of semi-solid primary phase. Solidification of semi-solid alloy is a course of change in fractal dimension.
关键词:
Semi-solid
,
初生相形貌
,
分形
,
A356铝合金 semi-solid, morphology of primary phase, fractal, A356 alloy
刘政
,
徐丽娜
,
余昭福
,
陈杨政
金属学报
doi:10.11900/0412.1961.2015.00496
利用稀土La对液态A356铝合金进行了细化处理, 并在电磁搅拌技术下制备了半固态A356-La铝合金浆料, 研究了稀土La和电磁搅拌对半固态A356铝合金初生相形貌的影响, 并用分形维数对其初生相形貌进行了表征. 结果表明, 添加适量的稀土La可有效改善半固态A356铝合金初生相的形貌, 无论是否经过电磁搅拌, 随着稀土添加量的增加, A356 铝合金的初生相形貌均呈先变好后恶化的演变规律, 当稀土La的添加量为0.4% (质量分数)时, 其初生α相的形貌和尺寸均达到最佳, 其平均等积圆直径为88.85 μm, 平均形状因子为0.78; 当稀土La的添加量相同时, 经过电磁搅拌作用的A356-La 铝合金初生α相的平均等积圆直径均比未经过电磁搅拌的更小, 其形状因子则相反, 均比未经过电磁搅拌的更大, 说明经过电磁搅拌的半固态A356铝合金初生α相比未搅拌过的更细小、圆整, 即经过电磁搅拌的初生α相形貌更佳, 如当La含量为0.4%时, 其平均等积圆直径由88.85 μm 降至84.14 μm, 平均形状因子由0.78升至0.81. 此外, 实际的合金凝固组织具有分形特征, 应用分形几何的原理来描述和分析半固态铝合金中初生相的形貌变化规律甚至初生相形成机理是完全可能的. 且不同工艺参数下所获得的半固态铝合金初生相形貌具有不同的分形维数, 随着半固态初生相由树枝状向颗粒状或球状变化, 其分形维数逐渐变小.
关键词:
A356铝合金
,
La
,
电磁搅拌
,
初生相形貌
,
分形
刘政
,
徐丽娜
,
余昭福
,
陈杨政
金属学报
doi:10.11900/0412.1961.2015.00496
利用稀土La对液态A356铝合金进行了细化处理,并在电磁搅拌技术下制备了半固态A356-La铝合金浆料,研究了稀土La和电磁搅拌对半固态A356铝合金初生相形貌的影响,并用分形维数对其初生相形貌进行了表征结果表明,添加适量的稀土La可有效改善半固态A356铝合金初生相的形貌,无论是否经过电磁搅拌,随着稀土添加量的增加,A356铝合金的初生相形貌均呈先变好后恶化的演变规律,当稀土La的添加量为0.4％(质量分数)时,其初生α相的形貌和尺寸均达到最佳,其平均等积圆直径为88.85 μm,平均形状因子为0.78;当稀土La的添加量相同时,经过电磁搅拌作用的A356-La铝合金初生α相的平均等积圆直径均比未经过电磁搅拌的更小,其形状因子则相反,均比未经过电磁搅拌的更大,说明经过电磁搅拌的半固态A356铝合金初生α相比未搅拌过的更细小、圆整,即经过电磁搅拌的初生α相形貌更佳,如当La含量为0.4％时,其平均等积圆直径由88.85μm降至84.14 μm,平均形状因子由0.78升至0.81.此外,实际的合金凝固组织具有分形特征,应用分形几何的原理来描述和分析半固态铝合金中初生相的形貌变化规律甚至初生相形成机理是完全可能的.且不同工艺参数下所获得的半固态铝合金初生相形貌具有不同的分形维数,随着半固态初生相由树枝状向颗粒状或球状变化,其分形维数逐渐变小.
关键词:
A356铝合金
,
La
,
电磁搅拌
,
初生相形貌
,
分形