金属学报(英文版)
Calcium treatment is nowadays a well-established method to improve steel castability and final properties e.g. machinability, toughness and surface quality. The effects of calcium are mainly based on its strong ability to form sulphides and oxides. The topic of the present paper concerns the basic mechanism and kinetics of the transformation process of alumina inclusions in steel when calcium introduced into the steel e.g. by wire feeding or powder injection.
To clarify the mechanisms model experiments were performed by studying reactions between Al2O3 and CaO in a laboratory furnace as well as by performing Ca treatments in an 8 kg induction furnace for Al deoxidised melt. The phases formed during the reaction between Al2O3 and CaO were examined by SEM-EDS, and the proposed reaction sequence of Al2O3CA6CA2CACAx(liquid) was discussed based on the experimental observations. The kinetics of the reaction of calcium with alumina inclusions were simulated by immersing alumina plates in a Ca treated steel melt in the induction furnace. Results were compared with observations of real inclusion transformation. Based on the results a kinetic model was proposed.
关键词:
Alumina inclusions
,
夹杂
,
机理
,
钙处理
,
动力学
冉孟伦
钢铁钒钛
介绍了采用LF炉工艺生产低硫高强耐候钢的炉外精炼处理技术及其综合应用,以及为经济高效生产该系列钢所开发的新材料 (钒钛微合金化包芯线) 的使用情况.生产实践表明,通过选择合理的脱硫工艺和采用新型的微合金化技术,LF炉工艺生产的低硫高强耐候钢的成品成分(S、V、Ti、N、Ca等)稳定,产品力学性能和耐腐蚀性均较为优良.
关键词:
耐候钢
,
炉外精炼
,
精炼渣
,
渣洗
,
吹氩
,
钙处理
,
碱度
郝鑫
,
王新华
,
王万军
钢铁
doi:10.13228/j.boyuan.issn0449-749x.20140149
通过工业试验研究了中厚板钢LF→钙处理→RH精炼过程中夹杂物的转变规律，并对钙处理过程夹杂物转变进行了热力学计算分析。结果表明：精炼过程钢中总氧质量分数降低，夹杂物数量密度降低，夹杂物平均尺寸升高；钙处理后夹杂物为CaO-MgO-Al2O3-CaS四元系；RH破空后夹杂物转变为CaO-MgO-Al2O3三元系，夹杂物中CaO质量分数降低，Al2O3质量分数升高；热力学计算表明，钙处理后钢液可直接生成CaS，也可与钙铝酸盐夹杂物反应生成CaS，RH破空后不能生成CaS。
关键词:
中厚板
,
炉外精炼
,
钙处理
,
夹杂物
,
洁净度
郭登仰
,
吴晓东
,
陈瑞泷
,
谈盛康
钢铁钒钛
通过热力学计算控制钢中喂钙量,把钙处理20CrMo钢中Al2O3变性为低熔点的12CaO·7Al2O3上浮去除,从而使钢中夹杂物满足评级要求；并用Thermo-Calc软件模拟钢液凝固过程中CA6、CA、CA2钙铝酸盐及MnS夹杂物的析出情况.用SEM对轧材中纺锤状夹杂物进行分析,少量夹杂物内核颜色较深,为Al2O3、CaS等夹杂,外层包裹的夹杂颜色较浅,为MnS夹杂.说明凝固过程中钢液中先析出的Al2O3、CaS等复合夹杂可以被后析出的MnS捕获作为其核心.
关键词:
钙处理
,
复合夹杂物
,
硫化锰
,
模拟
曹志刚
,
杜忠泽
,
许伟阳
,
颜慧成
,
俞海明
钢铁钒钛
简述了某炼钢厂将转炉冶炼的齿轮钢钢水倒运到电炉车间进行精炼的工艺管控过程.包括转炉的脱磷和 挡渣操作,精炼炉的送电制度,钙处理等影响质量的关键控制环节.同时也对轧制工艺进行改进,采用控轧控冷的TMCP技术,使圆钢轧材质量更加稳定.
关键词:
齿轮钢
,
转炉
,
脱磷
,
精炼炉
,
钙处理
,
TMCP控轧控冷
马文
,
孙彦辉
钢铁研究
在某钢厂现行的喂钙工艺条件下,对钙处理后夹杂物变性效果进行了分析.经过钙处理后,钢中非金属夹杂物的尺寸进一步降低,夹杂物的类型也有所改变.低熔点夹杂物所占比例由2.5％提高到60％以上,有效地防止了浇注过程中的水口堵塞.
关键词:
低碳铝镇静钢
,
钙处理
,
夹杂物
,
变性
陆巧彤
,
朱志远
,
王万军
,
王新华
,
徐国栋
钢铁
测定了集装箱板钢的高温力学性能,并比较钙处理和合金元素对其的影响.试验结果表明在1×10-3/s应变速率下,集装箱板钢连铸坯在凝固温度～600 ℃间存在两个脆性温度区域.细小的脆性夹杂物CaS优先析出并聚集在奥氏体晶界,使晶界进一步脆化,造成钙处理钢铸坯试样在第Ⅲ脆性区高温侧延塑性低于未经钙处理钢试样.为提高耐大气腐蚀能力而添加的合金元素P对其高温力学性能没有造成明显不利影响.同时结果表明集装箱板钢试样的零强度温度(ZST)在1 440～1 450 ℃左右,零延性温度(ZDT)在1 400～1 410 ℃左右.
关键词:
集装箱板钢
,
连铸
,
钙处理
,
高温延塑性
任子平
,
孙群
钢铁
针对用户对管线钢和汽车大梁钢钢种夹杂物球形变性的要求,研究了两种不同钢水精炼工艺条件下钢水中S含量、Als含量、钢水氧化性等因素对喂线效果的影响,目的是找出管线钢和汽车大梁钢喂线的影响因素,满足用户对轧材夹杂物变性的要求.
关键词:
管线钢
,
汽车梁
,
钙处理
,
夹杂物
,
变性