Chengtao LI
金属学报(英文版)
The corrosion behaviors of alloy 690 in 1 wt pct sodium hydroxide aqueous solutions with and without PbO were characterized by electrochemical measurements, including potentiodynamic polarization, electrochemical impedance spectroscopy and Mott-Schottky measurement. The results reveal that there is a great difference between the corrosion behaviors of alloy 690 in the two tested solutions. The corrosion current density in PbO-containing solution is higher than that in the solution without PbO, which may be attributed to the anodic dissolution of metallic lead deposited at the early stage of polarization. The electrochemical impedance of the specimen in PbO-free solution is higher than that in the solution containing PbO. The slope of the Mott-Schottky curve in Pb-containing solution decreases notably compared with that in the Pb-free solution, which can be interpreted by the chromium depletion in the duplex structure of passive films.
关键词:
Alloy 690
,
电化学阻抗谱
,
氧化铅
,
Mott-Schottky曲线
,
钝化膜
张杰刘奉令李伟华段继周侯保荣
金属学报
doi:10.3724/SP.J.1037.2010.00201
采用EIS, PC, SEM和EDS等方法, 通过在硫酸盐还原菌(SRB)的一个生长周期内测试Zn-Al-Cd牺牲阳极在不含和含SRB海泥中的腐蚀行为, 以对比研究海泥中SRB对其腐蚀行为的影响.EIS和PC测试结果显示, 实验初期, 试样在2种海泥中的腐蚀速率都快速增大,但由于SRB的大量增长, 其对试样的腐蚀作用不断增强, 所以在含SRB海泥中的腐蚀速率一直大于在不含SRB海泥的腐蚀速率; 实验后期, 由于SRB的大量死亡,其对试样的腐蚀作用已经十分微弱, 因此2者的腐蚀速率逐渐变得比较接近. SEM分析显示, 2种海泥中的试样表面都出现大量的腐蚀坑, 但含SRB试样表面的腐蚀程度更为严重. EDS结果显示含SRB试样表面的Zn和Al含量明显低于无SRB试样,说明了试样在含SRB海泥中的腐蚀溶解速度相对较大.
关键词:
硫酸盐还原菌
,
Zn–Al–Cd
,
marine sediment
,
electrochemical impedance spectroscopy
关永军
,
夏原
无机材料学报
doi:10.3724/SP.J.1077.2008.00784
通过调整电解液中硅酸钠的浓度, 利用等离子体电解氧化(PEO)技术在铝合金LY12表面制备了各种陶瓷涂层, 利用光学显微镜、XRD、电化学阻抗谱(EIS)对涂层的形貌、成分和涂层在NaCl溶液中耐腐蚀性能进行了研究. 结果表明: 提高电解液中硅酸钠的浓度可以使得涂层的总厚度增加, 但过高或过低的浓度都会导致致密层厚度的减薄. 当浓度为20g/L时, 所制备的涂层的成分以氧化铝为主; 当浓度为40g/L时, 涂层的成分主要是莫来石和氧化铝; 当浓度超过60g/L
时, 涂层的成分主要为非晶相. EIS的研究表明, 涂层耐腐蚀性取决于涂层中的致密层, 增加致密层的厚度可以提高PEO涂层的耐腐蚀性, 在中性、酸性、碱性腐蚀介质中, PEO涂层都显示出对基体良好的保护作用.
关键词:
等离子体电解氧化
,
ceramic coating
,
electrochemical impedance spectroscopy
,
corrosion mechanism
王贵领
,
张密林
,
赵辉
,
霍丽华
,
孙丽萍
无机材料学报
doi:10.3724/SP.J.1077.2006.01258
利用溶胶-凝胶法低温合成了钒掺杂硅酸盐氧基磷灰石La9(SiO4)6-x(VO4)xO1.5+0.5x (x=0、0.5 和1), 经XRD表征所得产品为磷灰石相. 以电化学阻抗谱研究了其导电性能, V的掺杂使电导率大大提高, 700℃C时La9(SiO4)5(VO4)O2电导率为5.23×10-3S·cm-1, 与未掺杂V的La9(SiO4)6O1.5相比提高了5倍. 氧分压PO2=105～1Pa时, La9(SiO4)6O1.5的电导率不改变, 而La9(SiO4)_5(VO4)O2的电导率则随着氧分压的降低而稍有增加, 表明钒的掺杂在体系中引入n型电子导电.
关键词:
溶胶-凝胶法
,
oxyapatite
,
interstitial oxygen ion conduction
,
electrochemical impe-dance spectroscopy (EIS)