ZHANG Jie
,
CAI Qing-wu
,
WU Hui-bin
,
ZHANG Kun
,
WU Bo
钢铁研究学报(英文版)
A new kind of Mn-Mo-Nb-Cu-B bainite steel which satisfied mechanical demands of E690 offshore plate steel was designed. The effect of two processes——thermomechanical control process (TMCP)+tempering (T) and thermomechanical control process (TMCP)+reheating and quenching (RQ)+tempering (T)——on microstructure and mechanical properties were studied by means of scan electron microscope (SEM), transmission electron microscope (TEM) and electron back scatter diffraction (EBSD). The results showed that optimal mechanical properties were available when tempering at 550 ℃ for both processes. The microstructure of the TMCP+T treated sample tempering in the range of 450 to 550 ℃ for 1 h did not change dramatically yet the lath in the TMCP+RQ+T treated sample merged together and transformed into polygonal ferrite. At the same time, the sub-structure of grain bainite transformed from lath to cell-shape to refine grains with tempering temperature mounting. Lots of sub-grain boundaries were located within bainite and adjacent bainite grain boundaries were high angle.
关键词:
offshore plate
,
low carbon bainitic steel
,
tempering
,
toughness
,
EBSD
LIU Yu-rong
,
YE Dong
,
YONG Qi-long
,
SU Jie
,
ZHAO Kun-yu
,
JIANG Wen
钢铁研究学报(英文版)
The microstructures and mechanical properties of Cr13 super martensitic stainless steel after different heat treatments were studied. The results show that the structures of the steel after quenching are of lath martensite mixed with a small amount of retained austenite. With the raising quenching temperature, the original austenite grain size increases and the lath martensite gradually becomes thicker. The structures of the tempered steel are mixtures of tempered martensite and reversed austenite dispersed in the martensite matrix. The amount of reversed austenite is from 754% to 2249%. After different heat treatments, the tensile strength, the elongation and the HRC hardness of the steel are in the range of 813-1070 MPa, 101%-212% and 2133-3237, respectively. The steel displays the best comprehensive mechanical properties after the sample is quenched at 1050 ℃ followed by tempering at 650 ℃.
关键词:
super martensitic stainless steel
,
quenching
,
tempering
,
structure
,
property
,
reversed austenite