Y. Li
,
J. P. Zhao
,
H. M. Huang
,
J. C. Han and S. Y. Du (Harbin Institute of Technology
,
Harbin 150001
,
China)
金属学报(英文版)
Ni0.35Zn0.65Fe2O4 ferrite was synthesized by SHS method. In the process of SHS, combustion temperature and velocity were the main process parameters , which were decided by the Fe content, grain size of the ferrite powder, relative density and the oxygen pressure. In this paper the effects of Fe content, grain size and oxygen pressure on combustion temperature and velocity were discussed. The relation between combustion temperature and magnetic permeability was also studied and the method of polynomial regression was used to establish the mathematical model of the relation.
关键词:
combustion temperature
,
null
,
null
,
null
,
null
,
null
姚军
,
张进秋
,
彭志召
,
张光磊
材料研究学报
研究了羰基铁粉中Fe含量和颗粒粒径对磁流变液的剪切屈服强度影响.结果表明,不同载液磁流变液的最大剪切屈服强度随着Fe含量的增大和软磁性颗粒粒径的增大而提高.推导了铁含量和粒径两个影响因素的比例关系,得到了颗粒粒径和Fe含量相互的权重关系,并进行了验证,发现Fe含量对磁流变液的剪切屈服强度的影响比颗粒粒径的影响更大.最后,分析了实验误差,证明实验结论是有效的.
关键词:
金属材料
,
磁流变液
,
Fe含量
,
颗粒粒径
,
剪切屈服强度
梁恩泉
,
黄森森
,
马英杰
,
张韧
,
雷家峰
,
柳洋
材料研究学报
doi:10.11901/1005.3093.2015.353
研究了Fe含量(0.03％-0.24％,质量分数)对Ti-6Al-4V ELI (TC4 ELI)合金力学性能的影响.利用EBSD对合金显微组织进行了表征,对3种不同Fe含量的TC4 ELI的拉伸性能、断裂韧性和疲劳裂纹扩展速率(da/dN)、蠕变性能进行了对比分析.结果表明:随着Fe含量增加,在保持断裂韧性不变的同时,TC4 ELI合金的抗拉强度获得提高;3种Fe含量的TC4 ELI合金在室温和200℃时的疲劳裂纹扩展速率相当,而400℃条件下提高Fe含量将增大da/dN;低于350℃时,提高Fe含量能够增强合金的抗蠕变能力,而高于350℃时,Fe的作用相反.分析可知:微量Fe在β相内富集,具有固溶强化作用,从而提高了合金的抗拉强度;高于350℃时,Fe具有加速扩散作用,加速了基体内原子和界面的运动,导致裂纹尖端塑性区内位错运动阻力降低,从而提高了da/dN,并且Fe加快了位错攀移的过程,提高蠕变速率,而低于350℃条件下,扩散运动减弱,Fe主要起到强化作用.
关键词:
金属材料
,
Ti-6Al-4V ELI
,
铁含量
,
断裂韧性
,
疲劳裂纹扩展
,
蠕变