曾潮流
,
张鉴清
,
吴维玟
,
郭建亭
金属学报
研究了Ｎａ_２ＳＯ_４沉积盐引起的Ｎｉ_３Ａｌ－Ｆｅ于７００一８２０℃空气中的腐蚀行为。结果表明，Ｎｉ_３Ａｌ－Ｆｅ遭受自持性的热腐蚀。热腐蚀的发生似可归因于Ｆｅ与Ｎａ_２ＳＯ_４反应的产物Ｎａ_２Ｏ与Ｎａ_２ＳＯ_４形成了Ｎａ_２Ｏ－Ｎａ_２ＳＯ_４共晶熔融盐，随后合金中Ｍｏ的氧化产物ＭｏＯ_３参与电化学阴极还原反应，从而引发合金快速的热腐蚀。此外，熔盐中Ｎａ_２ＳＯ_４与ＭｏＯ_３反应生成的ＳＯ_３导致了熔盐的高酸度和合金的内硫化，从而进一步加剧了腐蚀的进程。
关键词:
金属间化合物
,
Ni_3Al-Fe
,
Na_2SO_4 hot corrosion
,
null
J.T.Guo
,
S.H. Wang
,
H. Li
,
W.H. Lai and M.H.Tan(Institute of Metal Research
,
Chinese Academy of Sciences
,
Shenyang 110015
,
China Manuscript received 26 August 1996)
金属学报(英文版)
The isothermal oxidation behavior of Ni_3Al containtng 15 at.% Fe and NiAl containing 30 at.% Fe was studied for 100 h at 850, 950, 1050 and 1150℃, respectively. The results show that the oxidation kinetics of the two alloys obey a parabolic law at various temperatures and every parabolic curve possesses two oxidation rate constants. The morphology, microstructure and the chemical composition of the oxide scales were examined using optical metallography, X-ray diffraction analysis, scanning electron microscopy and electron probe microanalysis. The oxide scale of Ni_3Al containing 15 at.% Fe consists mainly of NiO, NiFe_2O_4, and FeAl_2O_4, and that of NiAl containing 30 at.% Fe consists of Fe_2O_3 and (Fe,Ni)Fe_2O_4, contrasting sharply to the oxide scales of pure Ni_3Al and NiAl which consist of Al_2O_3. The oxide scales on the surfaces of Ni_3Al and NiAl containing Fe are not too dense and not too cohesive to the matrix,so their oxidation resistance is not too good.
关键词:
:oxidation
,