周清
,
董绍明
,
张翔宇
,
丁玉生
,
黄政仁
,
江东亮
无机材料学报
doi:10.3724/SP.J.1077.2006.01378
以MTS/H2为前驱物, 采用强制脉冲CVI(FP-CVI)方法, 进行了在C纤维表面沉积SiC涂层的研究, 并探讨了其工艺过程. 结果表明, 在1000～1100℃和(5～25)kPa, 沉积得到的\beta-SiC具有明显的(111)面取向, 涂层均匀一致, 厚度可控. 在实验过程中, 随着单次驻留时间和脉冲次数的增加, 涂层厚度也随之增加, 涂层厚度与脉冲次数成非线性关系. 当脉冲次数为300时, C纤维表面沉积SiC层后其质量增加达到36.18%.
关键词:
C纤维
,
SiC coating
,
FP-CVI
Hejun Li Haibo Ouyang Lehua Qi Yulei Zhang Zhengjia Li Jianfeng Wei
材料科学技术（英文）
The influence of reaction temperature on the preparation of SiC coating on carbon fibers by the reaction of silicon monoxide with the deposited pyrolytic carbon (PyC) layer has been discussed. With rising reaction temperature, the thickness of SiC layer increases and the SiC grain is coarsening. The apparent activation energy for the synthesis of SiC layer is about 103.3 kJ/mol. The oxidation resistance of carbon fiber can be improved by the SiC/PyC layers significantly. The initial oxidation temperature of the SiC/PyC coated carbon fiber is about 300°C higher than that of the uncoated carbon fiber. The oxidation of the SiC/PyC coated carbon fiber is owing to the diffusion of oxygen through the cracks generated by the mismatch of thermal expansion.
关键词:
Carbon fiber
,
null
,
null
,
null
徐银丽
,
李树成
材料开发与应用
在高温有水氧化应力冲刷苛刻环境下,对SiC涂层C/C复合材料喷嘴开展了多种温度(630-1 200℃)、多种持续时间(10-60 s)的热震试验.结果表明:复合材料喷嘴共经受了50次热震,寿命为数十分钟;单次高温持续时间对复合材料喷嘴的寿命影响不大,而多次热震及应力冲刷是复合材料喷嘴破坏的主要因素;复合材料喷嘴的破坏是缓慢发生的,该材料是安全的.
关键词:
C/C复合材料
,
SiC涂层
,
有水氧化应力冲刷环境
,
热震
游小刚
,
谭毅
,
李佳艳
机械工程材料
通过原位反应在石墨坩埚切片表面成功制备了SiC涂层,并对其进行了循环热氧化试验,研究了SiC涂层的形成机理以及烧结温度和时间对涂层厚度的影响,并评价了涂层对提高石墨抗热氧化性及抗热冲击性的作用.结果表明:原位反应制备的SiC涂层厚度较为均匀;不同温度下的原位反应由不同的动力学过程控制;当温度接近硅熔点时,长时间加热能显著增加SiC涂层的厚度;烧结温度越高,SiC涂层的厚度越大;石墨表面的SiC涂层能够提高石墨基体的抗热氧化及抗热冲击性,且涂层厚度越大,作用越显著.
关键词:
原位反应
,
SiC涂层
,
石墨坩埚