The effects of the impurities Fe, Si, Na, K and a rare earth addition, Ce, on the intrinsic and extrinsic toughening levels have been investigated for the Al-Li based alloys 2090 and 1420. 29K reduction in the toughening level for the alloy 2090 with impurities 0.42% Fe+Si or 0.0132% Na+K i4 identified to be caused by the impurities.An improvement on the fracture toughness can be made by adding 0.05%-0.25% Ce to the alloy 2090. The reason behind this is that Ce microalloying can not only enhance both the intrinsic toughening level and the extrinsic toughening level but also suppress the embrittling behavior of the impurities. However, 0.06%-0.15% Ce microalloying fails to bring about any beneficial effect to the toughening level for the alloy 1420.
关键词:
Al-Li based alloy
,
null
,
null
,
null
张有慧
,
史大历
,
张林
,
杜敏
,
程国东
,
赵增元
腐蚀与防护
改变Al-Zn-In-Cd合金牺牲阳极杂质铁的含量,在20℃天然海水中研究其电化学性能.采用4d加速试验法测定了开路电位、闭路电位和电化学容量及电流效率,并采用循环伏安法研究了牺牲阳极的极化性能.结果表明,铁含量的变化对Al-Zn-In-Cd牺牲阳极开路电位以及闭路电位影响较小,而对牺牲阳极电流效率的影响较为显著.随着铁元素含量的增加,电流效率呈现下降趋势,但是在0.15％范围内仍可达到国标的要求,电流效率大于85％,且溶解形貌良好.循环伏安曲线表明,Al-Zn-In-Cd牺牲阳极极化性能良好.
关键词:
Al-Zn-In-Cd牺牲阳极
,
循环伏安法
,
电流效率
,
杂质
,
铁
郑宗文
,
于鸿垚
,
刘珍君
,
王凯
,
徐庭栋
,
胡祎罕娜
钢铁研究学报
doi:10.13228/j.boyuan.issn1001-0963.20130406
C-Mn钢的热塑性一直是材料学界的研究热点之一,但是产生热塑性恶化的机制一直不清楚.为了认识C-Mn钢热塑性恶化的产生机制,根据热循环引起的非平衡偏聚理论,分析了大量国内外关于C-Mn钢的热塑性试验数据,包括塑性槽的产生,塑性回复现象,高温拉伸试验过程中固溶处理温度与试验温度之间的温差效应,冷却速率对热塑性的影响以及孔洞的形成.数据分析和计算结果表明:C-Mn钢的热塑性恶化是由于杂质元素的非平衡偏聚引起的.
关键词:
热塑性恶化
,
C-Mn钢
,
杂质
,
晶界偏聚