ON THE SWERVING OF STRENGTH CURVE FOR STEEL 20Cr11MoVNbNB

FU Changpu ZHA NG Jinwang Shaanxi Mechanical Engineering Institute , Xi′an.ChinaPAN Jingda D U Wenfeng Beijing Heavy Electric Machine Works , Beijing , China

金属学报(英文版)

Study was made on the swerving of the curves of strength and hardness vs L-M parameter P=T(20+lgt)for steel 20Crl 1MoVNbNB aged at 550.600 and 650℃ for 0—5000 h,T being aging temperature in K and taging time in h.The swerving seems to be due to:(1)the coarsening of the mean size of principal precipitate M_(23)C_6,(2)the precipitation of Laves phase MoFe_2;(3)the decrease of Mo content in matrix and(4)the recovery and recrystallization of the matrix phase.

关键词: L-M parameter , null , null , null , null

Ti/Al比对GH984G合金长期时效过程中γ'沉淀相粗化行为及拉伸性能的影响

谭梅林 , 王常帅 , 郭永安 , 郭建亭 , 周兰章

金属学报 doi:10.11900/0412.1961.2014.00137

研究了2种Ti/Al比对新型Ni-Fe-Cr基合金GH984G在长达上万小时高温时效过程中γ'淀相的粗化行为及其拉伸性能的影响规律.结果表明:随时效温度从700℃升高至800℃,球形γ'沉淀相的粗化速率明显增大.在700和750℃长期时效过程中,高Ti/Al比和低Ti/Al比合金γ'沉淀相的粗化行为均符合Lifshitz-Slyozof-Wagner (LSW)理论,受扩散过程控制,高Ti/Al比合金中γ '沉淀相的粗化速率较高.800℃长期时效过程中,2种Ti/Al比合金γ'沉淀相的粗化行为偏离LSW理论.此外,时效时间小于3×103 h时,高Ti/Al比合金的γ'沉淀相长大较快,进一步延长时效时间,低Ti/Al比合金的γ'沉淀相长大速率较快.Ti/Al比对合金标准热处理态和700～800℃时效10480 h后合金的700℃拉伸性能无明显影响.通过选取合适的Ti/Al比,可以控制γ'沉淀相的粗化行为,增强合金组织稳定性.

关键词: Ni-Fe-Cr基合金 , 长期时效 , γ'沉淀相 , 粗化行为 , 拉伸性能

(W+Mo)/Cr比对铸造镍基高温合金时效组织和持久性能的影响

孙文 , 秦学智 , 郭建亭 , 楼琅洪 , 周兰章

金属学报 doi:10.11900/0412.1961.2014.00281

利用真空冶炼制备了不同(W+Mo)/Cr比(质量比)的铸造镍基高温合金,采用OM,SEM和TEM观察了合金试样的微观组织,研究了(W+Mo)/Cr比对合金组织演化和持久性能的影响.结果表明,(W+Mo)/Cr比对热处理态组织无明显影响,主要组成相为γ基体、γ相、初生M和晶界二次碳化物.长期时效期间,合金试样的组织演化主要包括γ相粗化、拓扑密排相(TCP)相析出、MC分解和晶界粗化.随(W+Mo)/Cr比降低,MC的热稳定性明显降低,晶界粗化程度升高,晶界碳化物发生了M6C→ M6C +M23C6→M23C6的转变.同时,TCP相的析出量明显减少.当(W+Mo)/Cr比为0.22时,无TCP相析出.另外,(W+Mo)/Cr比由高于0.55降低至0.37时,TCP相的种类由μ相转变为了μ与σ相共存.γ'相和晶界粗化及TCP相的析出是引起合金持久性能降低的主要原因.综合(W+Mo)/Cr比对合组织演化和持久性能的影响得出,(W+Mo)/Cr比约为0.37时,合金具有最佳的持久性能.

关键词: 镍基高温合金 , (W+Mo)/Cr比 , 长期时效 , 组织演化 , 力学性能