赵晓刚
,
龚维
,
冀克俭
,
邓卫华
,
周彤
,
李艳玲
高分子材料科学与工程
采用一种工艺简单、反应时间短、能耗低的合成工艺合成双酚A型聚芳醚酮.研究了单体配比、聚合反应时间、反应物浓度、溶剂对聚合反应的影响,最终确定合适的反应条件:单体摩尔比为1∶1,聚合反应时间为2.5h,溶剂为N-甲基吡咯烷酮,固含量为25％.同时研究了单体配比对聚合物热性能的影响,当单体摩尔比为1∶1时,聚合物的玻璃化转变温度和热失重温度都较高.
关键词:
双酚A型聚芳醚酮
,
合成
,
工艺
,
热性能
L.L.Wang
,
L.H.Zhao
,
W.Y.Hu
,
X.L.Shu
,
X.J.Yuan
,
B.W.Zhang and X.Sheng Department of Applied Physics
,
Hunan University
,
Changsha 410082
,
China
金属学报(英文版)
Manuscript received 24 June 1999 The Fe Al P alloy deposits were plated on copper sheets by electroless plating. The change law of the deposition rate, composition, surface appearance and structure for the deposits was studied by changing the metallic salt ratios (AlCl 3/AlCl 3+FeSO 4), the concentration of metallic salt AlCl 3 and reductant NaH 2PO 2. The optimum plating bath was obtained. It was found that the choices of ligand and reductant were the key of increasing Al content for the deposits.
关键词:
electroless Fe Al P plating
,
null
,
null
,
null
王磊
,
李智东
,
赵昆渝
材料热处理学报
以新鲜鸡蛋清作为复合络合剂,利用蛋清合成Ni0.6Cu0.4Fe2O4尖晶石铁氧体粉体.此方法反应条件温和、工艺简单、成本低廉,且容易控制.通过X射线衍射仪(XRD)和透射电子显微镜(TEM)分析样品的微观结构和形貌特征,并结合差热-热重联合分析仪(TG-DTA)研究样品的晶化过程,用激光粒度仪(LPSA)测量样品的粒度分布,用振动磁强计(VSM)测量样品在室温下的磁学性能参数.结果表明:Ni0.6Cu0.4Fe2O4氧体粉体较佳的制备工艺参数为采用两阶段式的烧结工艺:240℃保温lh,升温至440℃保温2h,最终介于520 ～ 550℃焙烧6h.在该条件下合成得到的Ni0.6Cu0.4Fe2O4铁氧体粉体为纳米级的、单相的,平均晶粒尺寸约为16.31 nm,平均颗粒尺寸约为2.19 μm,饱和磁化强度可达37 emu/g,平均矫顽力为68.53 Oe.
关键词:
Ni-Cu铁氧体
,
蛋清
,
低温烧结
,
粉体
,
工艺
陈险峙
,
周剑平
硅酸盐通报
以Bi(NO)3·5H2O和Fe(NO)3·9H2O为初始原料,KOH、NaOH和LiOH·H2O为矿化剂,乙二醇、浓度为65％ ～68％硝酸和氨水为辅助试剂,水热合成BiFeO3粉体.X-射线衍射图表明,当采用不同的矿化剂合成样品时,可以得到不同的铋铁系化合物,采用KOH为矿化剂时,更容易得到单相BiFeO3粉体;另外发现不使用辅助剂溶解硝酸铋,不仅容易得到单相BiFeO3粉体样品,而且工艺简单.在此基础上,进一步研究了KOH浓度、反应时间、反应温度和前驱物浓度对合成单相BiFeO3粉体的影响.
关键词:
BiFeO3粉体
,
水热法
,
工艺