The precipitation behaviour of Fe-Cr-Mo and Fe-Cr-W alloys during aging has been ex- perimentally studied.It was found that in the early stage of aging,a metastable R phase pre- cipitated in both alloys,it was transformed into stable μ-phase,Laves-phase,X-phase or σ-phase in the later stages.The crystallographic structure of metastable R-phase is rhombohedral with lattice parameters of a=0.9075 nm and α=74.45°.The chemical compo- sition of R-phase is Fe-(27.5—34.9)Mo-(0—25.5)Cr and Fe-(28.9—33.0)W-(9.36— 21.0)Cr in at.-% in Fe-Cr-Mo and Fe-Cr-W system,respectively.
关键词:
Fe-Cr-Mo alloy
,
null
,
null
,
null
刘世程
,
浜口由和
,
桑野寿
金属学报
研究了Fe-Cr-Mo、Fe-Cr-W合金的时效析出过程,发现在时效初期、两合金系中均有过渡R相析出,过渡R相为菱形点阵,α=0.9075nm,α=74.45°,其成分在Fe-Cr-Mo合金中为Pe-(27.5—34.9)Mo-(0—25.5)Cr,在Fe-Cr-W合金中为Fe-(28.9—33.0)W-(9.36—21.0)Cr(at.-％),时效后期,过渡R相分别向平衡相μ相、Laves相、χ相及σ相转变。
关键词:
Fe-Cr-Mo合金
,
Fe-Cr-W alloy
,
precipitation