金属学报(英文版)
The cleavage fracture mechanism of granular bainitie weld metal in 15MnVN steel has been investigated.SEM observation of a special specimen for revealing simultaneously fracture sur- face and microstructure shows that the cleavage of the weld is initiated by M-A constituent. The 95th percentile equivalent diameter of M-A constituent controls the cleavage fracture stress of the weld metal.
关键词:
granular bainite
,
null
,
null
,
null
许红梅
,
张宇
,
潘鑫
,
王银柏
钢铁
通过Gleeble热模拟方法研究了Ti和B对耐候焊丝钢的CCT行为影响规律.组织分析表明:在冷却速度为0.1～1℃/s时,将Ti质量分数从0.05％增加到0.10％后,相转变的开始和结束温度分别降低12和37℃,同时组织中TiN颗粒数量增加,也将产生M-A组元的临界冷却速度从0.5℃/s降低到0.2℃/s；继续添加0.002％B会进一步将相转变的开始和结束温度分别降低约26和60℃,同时增加相转变组织中的M-A组元的体积含量和尺寸,也将产生M-A组元的临界冷却速度从0.2℃/s降低到0.1℃/s.硬度数据表明:把Ti质量分数从0.05％增加到0.10％后,盘条强度增加约56 MPa;继续添加质量分数0.002％的B后,盘条强度将再增加78MPa.
关键词:
Gleeble热模拟
,
M-A组元
,
抗拉强度
,
耐候焊丝钢
,
含硼钢
李学达
,
林学强
,
孙建波
,
曹宁
材料热处理学报
doi:10.13289/j.issn.1009-6264.2016-X303
利用Gleeble热模拟实验机模拟了铁素体-贝氏体双相X100管线钢在不同的单道次热循环临界峰值温度(760℃和800℃)下生成的临界热影响区(ICHAZ)的组织,利用光学显微镜、扫描电镜、透射电镜等对显微组织进行了表征,尤其是对马氏体-奥氏体(M-A)组元的分布状态进行了研究.同时对不同峰值温度的样品在-20℃的冲击韧度进行了测试.结果表明,铁素体-贝氏体双相X100管线钢ICHAZ的冲击韧度较高,在760℃时平均为163 J,800℃时平均为201 J.800℃时的冲击韧度高于760℃,这是因为760℃时形成的M-A组元的分布较为连续,而加热至800℃时逆转组织含量更高,部分逆转组织转变为贝氏体,从而使得M-A组元的分布较为分散.贝氏体-铁素体双相组织X100管线钢的ICHAZ的冲击韧度明显高于传统的单相贝氏体组织管线钢,这是由于双相组织的ICHAZ处的M-A组元沿着铁素体-贝氏体边界形成,尺寸较小并且比较分散,因此对冲击韧度的危害程度显著降低.
关键词:
X100管线钢
,
临界热影响区
,
组织
,
冲击韧度
,
M-A组元