Jiansen NI
,
Hui XU
,
Mingyuan ZHU
,
Qiang LI
,
Bangxin ZHOU
,
Yu
,
a DON
材料科学技术（英文）
Nd8.5Fe74Co5Cu1Nb1Zr3Cr1B6.5 bonded magnets were prepared by melt-spun and subsequent heat treatment. Magnetic properties of Br=0.68 T, JHc=716 kA/m, (BH) max=77 kJ/m3 were achieved. The addition of Cr element shows to be significantly advantageous in reducing grain size and increasing the intrinsic coercivity.
关键词:
null
,
Nanocrystalline
,
Melt-spinning
,
Ma
Shihai GUO
,
Yanghuan ZHANG
,
Jianliang LI
,
Baiyun QUAN
,
Yan QI
,
Xinlin WANG
材料科学技术（英文）
A magnetic shape memory alloy with nonstoichiometric Ni50Mn27Ga23 was prepared by using melt-spinning technology. The martensitic transformation and the magnetic-field-induced strain (MFIS) of the polycrystalline melt-spun ribbon were investigated. The experimental results showed that the melt-spun ribbons underwent thermal-elastic martensitic transformation and reverse transformation in cooling and heating process and exhibited typical thermo-elastic shape memory effect. However the start temperature for martensitic transformation decreased from 286 K for as-cast alloy to 254 K for as-quenched ribbon and Curie temperature remains approximately constant. A particular internal stress induced by melt-spinning resulted in the formation of a texture structure in the ribbons, which made the ribbons obtain larger martensitic transformation strain and MFIS. The internal stress was released substantially after annealing, which resulted in a decrease of MFIS of the ribbons.
关键词:
Shape memory alloy
,
null
,
null
,
null