LUO Zhiping ZHANG Shaoqing Institute of Aeronautical Materials
,
Beijing
,
China LUO Zhiping
,
doctorate student P.O.Box 81-4
,
Beijing 100095
,
China
金属学报(英文版)
Microstructural studies have been made on the Mg-0.54Zr,Mg-5.68Zn and Mg-5.65Zn-0.50Zr alloys in the as-cast and homogenized states.The lenticular plates of {012}twins were found in three alloys.After homogenization,ZrH_2 phase formed in the Mg-0.54Zr alloy.The Mg_7Zn_3 phase of cubic structure with a=1.417 nm distributes at the grain boundaries of the Mg-5.68Zn alloy in the as-cast state and after homogenization,the Mg_7Zn_3 phase dissolves and the MgZn_2 phase occurs.The as-cast Mg-5.65Zn-0.50Zr al- loy consists of MgZn_3 phase and Zn-Zr compounds.After homogenization,the dispersed acicular MgZn_2 phase may precipitate.
关键词:
Mg-Zn-Zr alloy
,
null
,
null
许春香
,
王星
,
张金山
,
张照光
稀有金属材料与工程
研究了稀土元素Nd、Yb对Mg-5.5Zn-0.6Zr合金组织与性能的影响.结果表明:单独添加Nd或Yb元素后,试验合金的组织明显细化,同时在晶界处形成了γ ((Mg,Nd)Zn2)或γ((Mg,Yb)Zn2)三元稀土相;而复合添加Nd和Yb元素后,试验合金的组织不但没有细化,而且在晶界处形成了呈网状分布的γ((Mg,Nd+Yb)Zn2)四元稀土相,并且晶界变宽.经过T4固溶处理后,Mg-5.SZn-0.6Zr合金中的共晶组织完全溶入基体,而添加Nd、Yb元素后的Mg-5.5Zn-0.6Zr合金晶界处仍有未溶的化合物相存在.其中,添加Yb元素后的Mg-5.5Zn-0.6Zr合金经固溶处理后在晶界处形成了一种新的Mg-Zn-Yb三元球状颗粒相,其常温下的抗拉强度、屈服强度和伸长率分别达到了255.6 MPa、163.6 MPa和17.4%,这主要是因为加入稀土元素Yb后固溶处理产生了复合强化效果.在高温条件下,复合添加稀土元素Nb、Yb后的试验合金具有很好的热稳定性,但其高温塑性比较差.
关键词:
Mg-Zn-Zr合金
,
钕
,
镱
,
显微组织
,
力学性能
安迪
,
闫亮明
,
石阁
,
王昕
,
杨玉坤
,
王会廷
上海金属
在温度523~723 K和应变速率0.001~1 s-1范围内,利用Geeble-1500热模拟试验机,对均匀化态的Mg-5.9Zn-1.6Zr-0.9Y-1.6Nd合金进行等温压缩试验,并获得了应力应变曲线.研究了变形工艺参数对该合金流变应力的影响规律,计算了热变形激活能,建立了本构模型.结果表明,Mg-5.9Zn-1.6Zr-0.9Y-1.6Nd合金在变形过程中真应力随变形温度的升高而降低,随应变速率升高而升高,该合金的流变应力曲线可以用双曲正弦函数来描述.并求得该合金的热变形激活能为181.902 6 kJ/mol.
关键词:
Mg-Zn-Zr合金
,
热压缩
,
流变应力
,
本构模型