金属学报(英文版)
Four alloys TMS-75 (Base), Base+B, Base+C and TMD-103 (Base+B+C) with varying levels of B, C were directionally solidified (DS), and their weldability was investigated by bead-onplate electron beam welding. It was found that cracking occurred in the weld-metal, as well as in the heat affected zone (HAZ). Both γ/γ' and/or γ/carbide eutectic contributed to the weld-metal cracking, and theγ/γ' eutectic was found to be mainly responsible for cracking in HAZ. However, constitutional liquation of carbides seems to have made some contribution also.The B addition had a detrimental effect on HAZ cracking susceptibility, while C addition improved it appreciably even in the presence of B. In addition, no obvious differences were observed in cracking susceptibility of weld-metal in the four alloys. The cracking modes and mechanisms underlying the effect of B and C addition on weidability could be explained on the basis of microstructures of the four alloys.
关键词:
Ni-based superalloy
,
null
,
null
燕怒
,
韩晓琪
,
余泳华
,
游敏
,
彭文杰
机械工程材料
doi:10.11973/jxgccl201604003
在室温下使用超声疲劳试验机对GH4169镍基高温合金进行了105~108周次的疲劳试验,获得了S-N曲线并观察了疲劳断口形貌.结果表明:S-N曲线呈逐渐下降的趋势,没有出现疲劳极限,在超过107周次的循环后试样仍发生疲劳破坏;疲劳裂纹的萌生位置并未随S-N曲线的下降呈现出规律性,裂纹主要萌生于试样表面,少量萌生于试样内部;在超声疲劳载荷作用下试样同时存在塑性和脆性两种破坏方式.
关键词:
镍基高温合金
,
超高周疲劳
,
裂纹萌生
,
镍基合金
郑玉荣
,
吴新年
,
王晓民
中国材料进展
doi:10.7502/j.issn.1674-3962.2015.03.07
核心专利在一个专利群中处于节点和纽带的地位,是产业经济的核心.在调研大量国内外Ni基高温合金生产技术、合金产品、主要生产企业的基础上,通过常规选择方法、重要Ni基高温合金牌号对应的专利技术、重要生产技术对应的专利技术等方法选择了Ni基高温合金的核心专利技术.通过相关分析方法探讨了Ni基高温合金核心技术的主要分布区域、主要技术分布方向、核心技术的拥有企业、重点制备工艺等,绘制了Ni基高温合金核心技术及其产品的演进图谱,重点分析了Ni基高温合金制备技术、热障涂层技术、热处理技术、激光熔覆技术、合金修复技术等核心技术及其应用情况.在此基础上,对重点跟踪的企业以及他们的核心技术演进进行了探讨,并分析总结了近年来Ni基高温合金核心技术的研发方向.
关键词:
Ni基高温合金
,
核心技术
,
演进图谱
,
单晶
,
激光熔覆
,
热障涂层
,
铂族金属
薛茂权
稀有金属材料与工程
采用粉末冶金方法制各不同石墨含量(0%、3%、6%)的镍基高温合金,研究合金材料在900℃和100 h下的恒温氧化行为,用扫描电镜和X射线衍射对其氧化表面形貌和成分进行观察和分析.结果表明:石墨含量较低(0%,3%)时,镍基合金氧化动力学符合抛物线规律,表面氧化膜无剥落;石墨含量为0%的合金氧化膜由Cr2O3和NiCr2O4组成,石墨含量为3%的合金氧化膜由Cr2O3组成,当石墨含量增加到6%时,大量石墨的氧化分解导致合金初始氧化严重,石墨分解后的孔洞加速氧化反应过程.根据氧化膜的组成分析了合金的氧化机制.
关键词:
镍基高温合金
,
石墨
,
氧化动力学
,
氧化机制
封少波
,
张楠楠
,
罗兴宏
金属学报
doi:10.3724/SP.J.1037.2012.00037
为研究DZ483合金在凝固过程中的元素偏析行为对糊状区内液相密度的影响, 采用等温凝固结合水淬法对合金进行不同温度下的凝固实验. 利用OM 和SEM观察试样的凝固组织, 利用EDS测量固相和剩余液相的元素含量, 并根据剩余液相的成分计算其密度. 结果表明, DZ483合金的开始凝固温度略低于1335℃, 在1325℃液相中开始析出富含Ta和Ti的MC; W和Co为负偏析元素, Mo, Ta和Ti为正偏析元素, 而 Al和Cr几乎不发生偏析; 剩余液相的密度随温度降低基本呈下降趋势, 但在1325至1315℃之间有所回升. 计算结果表明, 温度对液相密度的影响很小,合金元素的偏析对液相密度的影响占主要地位. 其中, Mo和Ta的偏析导致液相密度增加, 而Ti和W的偏析导致液相密度明显降低. 各合金元素的偏析对密度变化的贡献由大到小顺序为: Ti>Ta>W>Cr>Mo>Al>Co. MC的形成消耗了大量的Ti和Ta, 对合金元素的偏析造成一定的影响, 从而导致液相密度在1325至1315℃ 之间有所增加.
关键词:
镍基高温合金
,
freckle
,
segregation
,
density
魏振伟
,
刘昌奎
,
顾玉丽
,
陶春虎
航空材料学报
doi:10.11868/j.issn.1005-5053.2015.5.011
对GH536合金焊接接头的硬度进行测试和分析,对母材及焊接接头进行室温和500℃拉伸试验,并分析了断裂特征,分析了母材和焊接接头不同区域的断裂韧度.结果表明:热影响区硬度未见明显变化,与母材一致;从熔合线到焊缝中心,由于枝晶变细,显微硬度逐渐升高.焊接接头整体室温拉伸强度、屈服强度和断后伸长率分别为810MPa,392MPa和30％,达到了母材的99.6％,99.7％和93.8％;在500℃时,接头整体抗拉强度、屈服强度和断后伸长率分别为678MPa,300MPa和26％,达到了母材的98.1％,96.8％和78.8％;GH536合金焊接接头具有良好的力学性能.在熔合区组织不均匀性最为严重,熔合区是GH536合金焊接接头的薄弱环节.在室温和500℃,母材及焊接接头的断裂方式均为塑性断裂.
关键词:
镍基高温合金
,
钨极氩弧焊
,
显微硬度
,
拉伸性能
,
断裂韧度
,
裂纹尖端张开位移
闵志先沈军冯周荣王灵水刘林傅恒志
金属学报
doi:10.3724/SP.J.1037.2010.00305
采用定向凝固技术结合液淬法对DZ125合金平界面和枝晶生长条件下溶质的偏析行为进行了研究, 通过EPMA定量测定γ基体中各元素的溶质含量和淬火平界面两侧固相和液相中的溶质含量, 分别获得了溶质再分配后固相中的溶质分布状态及溶质分配系数. 结果表明, 平界面生长条件下,液相中的熔体流动使溶质再分布始终处于非稳态. Al, Ti, Ta, Mo和Ni元素的溶质分配系数小于1; 而W, Cr和Co元素的溶质分配系数大于1, 溶质分布状态满足Scheil模型. 枝晶与平界面生长的溶质偏析行为基本一致, 然而,固相反扩散显著降低了枝晶生长过程中的溶质偏析.
关键词:
镍基高温合金
,
solute partition coefficient
,
segregation
,
directional solidification
郭领军
,
李贺军
,
郭琛
,
李克智
,
冯涛
稀有金属材料与工程
通过包埋工艺在C/C复合材料表面制备了改性SiC涂层.采用Ni-Ti粉末作中间层连结材料,利用真空热压扩散工艺成功制备了SiC涂层改性C/C复合材料与GH3128镍基高温合金的连接样件.借助X射线衍射仪、扫描电子显微镜、能谱分析仪和材料万能试验机,研究了SiC涂层改性C/C复合材料与GH3128镍基高温合金连接接头及其界面的元素分布、微观结构及力学性能.结果表明,在C/C复合材料表面制备SiC涂层,不仅充分改善了C/C复合材料对Ni-Ti中间层连结材料的润湿性,而且还有效缓解C/C复合材料与GH3128连接界面因热膨胀不匹配而造成的热应力.经过SiC涂层改性处理的连接接头,其室温剪切强度可达22.49 MPa；而没有经过SiC涂层改性处理的连接接头,其室温剪切强度几乎为零.
关键词:
连接
,
C/C复合材料
,
镍基高温合金
,
剪切强度
,
微观结构
韩志宇
,
曾光
,
梁书锦
,
陈小林
,
张鹏
,
张平祥
中国材料进展
doi:10.7502/j.issn.1674-3962.2014.12.05
粉末高温合金是先进航空发动机关键热端部件的优选材料,先进的粉末制备技术是获得高品质高温合金粉末、保证合金件质量的关键技术.近年来,我国在粉末高温合金的研发和生产技术方面都取得了突破性进展,成功研发出新一代粉末高温合金,形成了成熟的粉末高温合金生产工艺.在粉末制备技术方面,通过对高纯净母合金熔炼技术、先进雾化制粉技术和电选分离技术的深入研究,进一步发展了粉末纯净化制备技术,满足了我国航空发动机领域对粉末高温合金关键零部件的需求.简要回顾了国内外粉末高温合金的发展历程,分析了粉末高温合金中的缺陷来源及其对合金性能的影响,概述了我国镍基高温合金粉末制备技术的发展情况,讨论了未来高温合金粉末及其关键制备技术的发展方向.
关键词:
Ni基高温合金
,
粉末制备
,
AA法
,
PREP法
,
粉末纯净化