W.H. Tian*
金属学报(英文版)
A transmission electron microscopy (TEM) investigation has been performed on the dislocation pinning in L12-ordered Ni3(Al,Ti) containing disordered γ precipitates. The morphology of defor?鄄mation induced dislocations in the γ' base alloys containing fine dispersion of disordered γ was investigated by means of weak-beam electron microscopy. The superdislocations are strongly at?鄄tracted to the disordered particles and dissociate on the (111) plane in the γ particles, while they dissociate on the (010) plane in the γ' matrix. The disordered γ precipitates play an important role as a pinning point during the cross-slip of superdislocations from (111) to (010) planes in the γ' matrix and restrain the cross-slip of superdislocations. The interaction of superdislocations with disordered particles causes the formation of superkinks, jogs and closed loops.
关键词:
superdislocation
,
precipitates
,
attractiv