李处森
,
杨院生
中国腐蚀与防护学报
叙述了碳气氛温度、金属材料种类及表面状态、构成碳源的气体种类、比例及流速等因素对金属材料结焦行为的影响，介绍了催化结焦的引发机理及其应用。然后以FeCrNi合金为例，分别介绍了内部渗碳和金属粉化这两种渗碳行为，并叙述了温度、碳气氛、合金材料晶体结构及成分构成的影响。最后分析了结焦和渗碳的关系，并介绍了添加结焦抑制剂、调整金属材料结构及成分构成、表面涂层化3种防护对策。
关键词:
金属材料
,
coking
,
carburizing
,
metal dusting
XIA Lifang MA Xinxin Harbin Institute of Technology
,
Harbin
,
China
金属学报(英文版)
This paper deals with the cause of intergranular fracture occurred in the retained austenitic region in plasma carburized layer.The results show that the presence of retained austenite, which has a good effect on the impact toughness,has no relation to this embrittlement.Analy- sis by Auger electron spectroscopy shows that the impurities S and P segregate at the grain boundaries is the main reason of the intergranular embrittlement in carburized layer. However,the segregation of P and S can be removed by reheating and quenching treatment.
关键词:
plasma carburizing
,
null
,
null
,
null
黄斌
,
朱洪武
,
杨忠
,
周乐育
,
刘雅政
材料热处理学报
通过固体渗碳试验研究了加热温度对钎具用钢22Si2MnCrNi2MoA渗碳层的影响,分析了渗碳温度-碳浓度-显微硬度-残留奥氏体的关系以及残留奥氏体的控制措施.结果表明:当渗碳时间为6h时,随着渗碳温度的升高,渗碳层的碳浓度逐渐增加,碳浓度分布梯度越来越平缓.22Si2MnCrNi2MoA钢渗碳层的显微硬度-碳浓度关系符合正态分布.在渗碳处理过程中,为了使渗碳表层获得硬度很高的马氏体组织,22Si2MnCrNi2MoA钢渗碳层表面碳浓度应该控制在0.80％ ～0.90％之间.当表面碳浓度超过0.80％～0.90％时,渗碳完成后需采取后续的工艺措施来消除已经存在的残留奥氏体,如采用长时间自然时效或深冷处理等.
关键词:
钎具用钢
,
22Si2MnCrNi2MoA
,
渗碳
,
残留奥氏体
,
加热温度
薛文斌
,
金乾
,
刘润
,
金小越
,
王彬
,
杜建成
中国有色金属学报
以50%~90%(体积分数)甘油水溶液为电解液,研究304不锈钢表面液相等离子体电解快速渗碳工艺;分析不同甘油浓度和电压下渗碳层的显微组织、相组成和显微硬度.结果表明,随甘油浓度的提高,渗透电压上升,渗碳层厚度增加,渗碳层硬度增大,最大硬度达到762HV;且渗碳层中固溶碳的奥氏体(γC)含量急剧增加,但碳化物含量降低.在80%(体积分数)甘油水溶液和电压350 V工艺条件下获得的渗碳层质量较好.
关键词:
甘油
,
不锈钢
,
液相等离子体电解渗
,
渗碳