Y. Li
,
J. P. Zhao
,
H. M. Huang
,
J. C. Han and S. Y. Du (Harbin Institute of Technology
,
Harbin 150001
,
China)
金属学报(英文版)
Ni0.35Zn0.65Fe2O4 ferrite was synthesized by SHS method. In the process of SHS, combustion temperature and velocity were the main process parameters , which were decided by the Fe content, grain size of the ferrite powder, relative density and the oxygen pressure. In this paper the effects of Fe content, grain size and oxygen pressure on combustion temperature and velocity were discussed. The relation between combustion temperature and magnetic permeability was also studied and the method of polynomial regression was used to establish the mathematical model of the relation.
关键词:
combustion temperature
,
null
,
null
,
null
,
null
,
null
卜昌盛
,
庄亚明
,
刘道银
,
陈晓平
工程热物理学报
在二维热态可视化流化床实验平台上深入研究了O2/N2和O2/CO2气氛下单个煤颗粒燃烧特性.实验中流化床床温为1088 K,O2浓度为10％～40％,拟球形煤颗粒粒径为6 mm,两根热电偶分别记录煤燃烧过程中颗粒中心及表面温度的变化规律.实验结果表明:O2/CO2气氛下O2扩散速率低于O2/N2气氛,使得煤颗粒的平均表观燃烧速率、升温速率及温度峰值降低,燃尽时间延长;提高O2浓度后燃烧特性得以改善.为获得与空气气氛相近的燃尽时间,O2/CO2气氛下O2浓度约需25％,但O2浓度需30％才可达到和空气气氛相近的燃烧温度峰值.
关键词:
富氧燃烧
,
流化床
,
煤颗粒
,
燃烧温度
,
燃尽时间
张立
,
肖国庆
,
丁冬海
,
殷汉青
,
刘科燕
人工晶体学报
以金属Al粉和B2O3粉为原料,采用自蔓延高温合成法(SHS)制备AlB2-Al2O3复合粉体.采用X射线衍射仪、扫描电镜和能谱仪分析手段,对所制得的复合粉体进行了表征.研究了Al粉粒度(100目、300目和600目)对自蔓延高温合成方法制备AlB2-Al2O3复合粉体的燃烧学、相组成及微观结构的影响.结果表明:铝粉粒度越小,燃烧温度越高、燃烧波速度越快,复合粉体中AlB2相含量增加,实验测得600目铝粉反应的燃烧温度为2060K,燃烧波速度为2.08 mm/s.复合粉体以AlB2和Al2O3为主晶相,显微结构为数量较少、粒径约5μm的AlB2粉弥散分布于粒径约2 μm的Al2O3和Al的混合粉中.
关键词:
自蔓延高温合成
,
AlB2-Al2O3复合粉体
,
粒度
,
燃烧温度
,
燃烧波速