The relative ratio of fatigue resistance to creep resistance of materials varies with test temper- ature.As the temperature decreases,the creep resistance,since it is a thermal activation pro- cess,becomes relatively larger than fatigue resistance.Therefore the fatigue damage becomes predominant,and results in expansion of fatigue fracture region(region F),and shrinkage even complete elimination of creep fracture region(region C).A materials parameter Ω can be defined to estimate the temperature at which the creep fracture region is completely de- pressed.This phenomenon could be understood on the basis of the integrated model of compet- itive and cumulative models of fatigue creep interaction.
关键词:
creep fracture
,
null
,
null
,
null
艾素华
,
V.LUPINC
,
M.MALDINI
金属学报
本文研究了〈001〉取向的CMSX—2,SRR99和RR2000三种单晶镍基高温合金,从750-1000℃温度范围和从150—680MPa应力下的蠕变断裂特征;用扫描电镜对上述各种实验状态下的蠕变断口和纵向剖面进行了详细观察。结果表明:单晶的蠕变断裂具有明显的晶体学特征,蠕变裂纹总是从已有的铸造的显微疏松处萌生;对于含碳量较高的材料,碳化物及其与基体的界面也是裂纹萌生的有利位置;这些已萌生的裂纹在外加应力轴垂直的(001)面上各向异性地扩展,直到由于承载截面的逐渐减小而导致最终破坏。虽然在较高的实验温度下,断口被强烈地氧化,但是蠕变断裂特征没有改变,在对三种材料断口上(001)面的大小和面积分数的测量和计算表明,用面积分数来表征蠕变损伤程度是可行的。
关键词:
单晶镍基高温合金
,
micropore
,
crack initiation
,
creep fracture
侯介山
,
张玉龙
,
郭建亭
,
冀
,
光
,
周兰章
,
叶恒强
金属学报
研究了铸造镍基高温合金K44在850---900℃, 225---380 MPa的高温拉伸蠕变行为.结果表明, 实验合金蠕变曲线具有较短的初始阶段和较长的加速阶段, 加速阶段较长是由于筏形化的r’粒子和位错相互作用促成的. 加速蠕变为应变软化阶段时, 可以由关系式来描述. 蠕变断裂数据遵守Monkman--Grant规律, 裂纹起源于晶界或枝晶界的空洞.
关键词:
镍基高温合金
,
high temperature creep
,
creep fracture
张超
,
丁兆波
,
徐玉松
机械工程材料
研究了Cu-0．2Zr（质量分数／％，下同）合金和Cu-3Ag-0．5Zr合金在700，800，900K下的拉伸蠕变行为，并分析了两种合金的蠕变机理。结果表明：铜一锆合金的抗蠕变性能优于铜-银-锆合金的；在700K的蠕变区，位错粘滞滑移是两种合金蠕变过程的控制机制，在800K的蠕变区，两种合金的蠕变过程主要由晶界扩散机制所控制；高温蠕变断裂时两种合金均表现为韧性沿晶断裂，并存在二次裂纹，铜一锆合金断口的孔洞较多，两种合金的蠕变断裂数据符合Monkman-Grant关系。
关键词:
Cu-0．2Zr合金
,
Cu-3Ag-0．5Zr合金
,
高温拉伸
,
蠕变断裂