钱匡武
,
李效琦
,
肖林钢
材料研究学报
研究了晶粒尺寸对Cu-32Zn 合金锯齿屈服的影响。实验表明:(1)在半经验公式ρ_m=N·ε~β及C_v=K·ε~m 中的β及m 随晶粒度加大而增大;(2)获得了四种不同类型的锯齿波;(3)出现锯齿波的温区按临界应变量ε_c 随温度升高而分别减小、为0及增大而分成三个区段;(4)随着晶粒度的增大,ε_c 变大;出现锯齿波的温度范围扩大;三个温区中的两个温度点移向高温区;锯齿波的波幅减小。上述结果可用ρ_m 及C_v 和晶粒尺寸的关系及根据大量位错的集体行为和溶质原子与位错的弹性交互作用的模型来解释。
关键词:
锯齿屈服
,
PL effect
,
dynamic strain aging(DSA)
,
grain size.
CHEN Wenzhe QIAN Kuangwu FuZhou University
,
Fuzhou
,
Fujian
,
China Lecturer
,
Dept.of Mechanical Engineering
,
Fuzhou University
,
Fuzhou
,
Fujian
,
China
金属学报(英文版)
The effect of various dynamic strain aging(DSA)pre-treatment processes on pure bending fatigue strength of an 18-8 austenitic stainless steel was investigated.The results show that DSA pre-treatment processes increase remarkably the fatigue strength and the strengthening effects increase with increasing pre-strain temperature and pre-strain.The fatigue limit of specimens pre-treated by DSA is 87% higher than that by solution treatment,and 20% high- er than that by cold-working.TEM observations show that the uniform and stable dislocation networks with high density formed after DSA pre-treatment,which suppress effectively the initiation and propugation of fatigue cracks and increase the fatigue strength of materials.
关键词:
dynamic strain aging(DSA)
,
null
,
null
金丹
,
李江华
,
田大将
材料研究学报
doi:10.11901/1005.3093.2015.196
进行了316L不锈钢在600℃不同应变条件下的单轴低周疲劳实验.结果表明,材料在三个应变范围下均表现出了动态应变时效(DSA)现象,采用“应力跌幅”的概念比较了不同应变范围的锯齿屈服程度,通过可动位错与扩散的溶质原子间不同形式的交互作用分析了此现象,讨论了最大应力跌幅的循环硬化及循环软化的相关性.DSA现象有明显的循环周次相关性,循环初期DSA现象明显,随后逐渐减弱甚至消失,但是在失效前DSA现象再次出现,气团形式的不同造成了不同循环周次下DSA现象的差异.在低应变范围DSA现象仅表现出了A型锯齿波,在高应变范围不同周次及同一周次的不同阶段波型表现为A、B、A+B、C及B+C型.最后,采用SEM分析了疲劳断口的裂纹源区和扩展区.
关键词:
金属材料
,
316L不锈钢
,
动态应变时效(DSA)
,
应力跌幅
,
锯齿波
,
原子气团