Ni-Cr System solar selective thin solid films were prepared by d.c. magnetron reactivesputtering under the atmosphere of O2 and N2. Ni-Cr alloy was chosen as targetmaterial and copper sheets as substrate. Using SEM, Spectrophotometer and Talystepto analyze the relations between the selective characteristic and the structure, theformation and the thickness of the thin films. The aim is to obtain good solar selectivethin films with high absorptance and low emittance, which is applied to flat plate solarheat collectors.
关键词:
solar selective thin film
,
null
,
null
,
null
高东山
,
房正刚
,
陆春华
,
倪亚茹
,
许仲梓
功能材料
doi:10.3969/j.issn.1001-9731.2015.05.007
以柠檬酸为络合剂,采用络合溶胶-凝胶法合成钙钛矿型氧化物 Sm0．5 Sr0．5 CoO3－δ(SSC5),并通过TG-DSC、XRD、SEM、XPS和UVPC对其进行了表征.结果表明,在1200℃保温6 h后合成出粒径约为1μm左右的 SSC5粉体.Sr2＋取代 Sm3＋导致了体系中Co离子的价态发生 Co2＋→Co3＋→Co4＋转变,且在SSC5表面出现了大量的吸附氧.SSC5陶瓷片的吸收率(αS)和发射率(εT)分别为0．71和0．19,具有良好的光谱选择性.
关键词:
溶胶-凝胶法
,
SSC5
,
钙钛矿
,
发射率
韦玲
,
陆依
,
房正刚
,
张荣
,
陆春华
,
许仲梓
人工晶体学报
采用固相法制备(Sm1-xBix)05Sr05CoO3-δ (0≤x≤0.5),研究不同Bi3+掺杂浓度对材料的晶体结构、表面形貌与光学性能的影响.结果表明,当掺量0≤x(Bi3+)≤0.2,材料为单一纯相的钙钛矿结构;当掺量0.3≤x≤0.5,材料主相仍保持着钙钛矿结构,同时出现杂相CoO与Sr0.5CoBi0.5Ox.(Sm1-xBix)05Sr05CoO3-δ平均粒径随着Bi3+掺量的增加由1.98 μm增大为9.77 μm,晶粒形状由多边形状变为方块状;光学测试表明,随着Bi3+浓度的增加,材料的光学吸收率由0.73增大到0.87,发射率由0.34增大到0.80.
关键词:
固相法
,
太阳吸收率
,
发射率
,
Sm0.5Sr05CoO3-δ