J.X.Dong
,
M.C.Zhang
,
Y.P.Zeng
,
X.S.Xie
金属学报(英文版)
The freckle formation and their phase characterizatics in freckle areas were investigated by means of microstructure analysis approaches and a thermodynamic equilibrium phase calculation method in an lnconel 625 alloy. These results show that in freckle areas a large number of M6C, MC, Laves and 8 p...
关键词:
freckle
,
null
,
null
J.X.Dong
,
M.C.Zhang
,
Y.P.Zeng
,
X.S.Xie
金属学报(英文版)
The freckle formation and their phase characterization in freckle areas were investigated by means of microstructure analysis approaches and a thermodynamic equilibrium phase calculation method in a Ni-Cr-Mo-Fe-W alloy. These results show that in freckle areas a large number of M6 C, u and P phases ...
关键词:
freckle
,
null
,
null
田俊
,
刘岩
,
成国光
钢铁
对H13钢试样进行了退火试验,对退火前后试样进行了硬度测试及扫描电镜和能谱分析。分析了H13钢热轧材硬度不均匀性的形成原因。结果表明,低倍＂黑斑＂区域硬度平均值为91.43HRB,比正常区域高7.53%;＂黑斑＂区域主要由＂白斑＂和＂黑色质点＂组成,＂白斑＂化学成分主要是铁,＂黑色质点＂主要成分为合...
关键词:
H13钢
,
黑斑
,
碳化物
,
硬度
,
退火
马德新
金属学报
doi:10.11900/0412.1961.2015.00379
通过实施工业条件下的定向凝固实验, 对复杂形状的高温合金铸件中的雀斑进行了检测和分析, 揭示了这种凝固缺陷产生的几个新特点. 结果表明, 雀斑易于产生在铸件的棱角部位而不是平滑表面上, 称之为棱角效应; 铸件外形台阶式地突然扩张和缩小会分别抑制和促进雀斑形成, 称之为台阶效应; 雀斑易于产生在向内倾斜而不是向外倾斜的铸件表面上, 称之为斜面效应; 叶片曲率为正的外凸曲面出现严重的雀斑缺陷, 而曲率为负的内凹曲面却毫无雀斑, 此现象称之为曲率效应. 实验中还发现雀斑不但出现在铸件的外表面, 插入型芯也会诱导铸件内部雀斑的产生, 这说明糊状区的液体流动具有强烈的附壁效应, 不管这种壁面是处在铸件外部还是内部. 通过分析可以确认, 正是这种附壁效应在各种具体形状特征下发挥作用, 导致了上述关于雀斑生成的各种效应.
关键词:
高温合金
,
雀斑
,
定向凝固
,
铸件
高斯峰
,
刘林
,
胡小武
,
葛丙明
,
张军
,
傅恒志
材料科学与工程学报
本文简述了近年来定向和单晶镍基高温合金凝固过程中雀斑缺陷的研究进展,具体论述了雀斑缺陷的形成机制以及雀斑的预判模型,并从合金成分、凝固参数(抽拉速率和温度梯度)、凝固界面形态以及试样形状和尺寸等方面分析和论述了这些因素对雀斑缺陷形成的影响,最后对未来镍基高温合金中雀斑缺陷的研究方向进行了探讨和展望.
关键词:
镍基高温合金
,
雀斑
,
定向凝固