L. Zhou
,
X.Q. Wei
,
N.G. Zhou
金属学报(英文版)
Molecular dynamics simulations of high temperature annealing of copper bicrystals
have been carried out. The bicrystals have planar grain boundaries, and the gain
size varies in nano range. An EAM(Embedded Atom Method) potential of FS type is
used for calculating the interatomic forces. The results show that in nanocrystalline
copper, GB migration driven by inter-GB reaction can take place. A critical grain
size is identi¯ed, below which the inter-GB reaction becomes strong enough to trigger
GB motion, which accelerates rapidly and leads to annihilation of the grain bound-
aries. The critical size is found to be 16 atomic radii. A \through intermediate grain
mechanism" is identi¯ed for the nano-grain boundary motion observed, which is never
reported for GB migrations of conventional polycrystalline metals.
关键词:
grain boundary migration
,
null
,
null
苑少强
,
杨跃辉
,
梁国俐
材料导报
doi:10.11896/j.issn.1005-023X.2015.04.025
利用热模拟技术、金相观察及定量统计,通过分析Fe-40Ni-Ti合金快速升温过程中试样不同部位的晶粒长大规律,模拟研究了焊接过程中奥氏体晶粒的长大行为.结果表明:温度最高的中心线附近晶粒长大显著,5 s内温度达到1350℃时,其尺寸达到了180 μm;而距离中心线4 mm处的热影响区及母材(试样端部)晶粒变化不大,在80 μm左右.金相观察发现TiN颗粒对晶界迁移产生了明显的阻碍作用.
关键词:
热模拟
,
Fe-40Ni-Ti合金
,
热影响区
,
TiN颗粒
,
晶界迁移
罗志荣
,
卢成健
,
高英俊
,
易施光
兵器材料科学与工程
采用晶体相场方法模拟U形半环双晶的演化过程,讨论晶界曲率对体系自由能及晶界迁移的影响.结果表明:在双晶演化过程中体系自由能不断降低直至演变成单晶,且晶界曲率越大自由能降低越快;半环晶粒在收缩过程中晶界迁移具有稳态性质,且迁移速度正比于晶界曲率.
关键词:
晶界迁移
,
位错
,
晶界曲率
,
晶体相场方法
苑少强
,
郁春锋
,
杨跃辉
,
郝斌
材料热处理学报
利用金相观察、定量统计及透射电子显微镜分析,研究了含Ti和无Ti的Fe-40Ni合金在高温等温过程中的晶界迁移行为.结果表明:Fe-40Ni-Ti合金原始试样中存在两种析出,分别是凝固过程中形成的尺寸较大的TiN颗粒及锻压过程中形成的应变诱导析出相,尺寸为10 nm左右.在1100℃等温30 min后,没有发现应变诱导析出相存在.直接观察结果则显示粗大的TiN颗粒对晶界迁移有明显的阻碍作用,以类似于位错绕过析出颗粒的Orowan机制绕过TiN颗粒,其主要原因可能是高温时晶界自由能明显各向同性,只有直接面对析出相的局部晶界受到析出相的阻碍,能够发生大曲率弯曲,晶界表现出较强的"柔性",此时析出粒子必然无法对其运动产生强烈的阻碍作用.
关键词:
Fe-40Ni-Ti合金
,
晶界迁移
,
TiN析出