(N~++IP)-TiN复合涂层界面显微硬度分布

金柱京 , 于力 , 于志明 , 戴少侠 , 徐家寅

金属学报

由离子氮化与离子镀复合工艺在A_3钢基材上获得(N~++IP)-TiN复合涂层。其涂层与基格界面的显微硬度随着从涂层表面到基材距离的逐渐增加而缓慢降低。经X射线相分析及电子探针元素分析认为。主要是由于IP-TiN膜与基材之间存在着离子氮化层(εFe_3N-Fe_2N相和Fe_4N相)所致。

关键词: 显微硬度 , composite coating , inierface , ion-plating , ion

Ni基体磁控溅射离子镀Al膜的电镜观察

万立骏 , 陈宝清 , 郭可信

金属学报

利用横截面电镜样品,对Ni基体磁控溅射离子镀Al膜进行了透射电镜观察。研究了不同工艺条件下镀膜的组织形态,相结构以及相分布。镀覆5min时,在Ni基体和镀Al膜交界处,发现一个Al-Ni系中迄今未见报道的未知相。经电子衍射分析其为体心四方点阵,a=b=0.588nm,c=0.480nm。研究了随时间变化的镀膜组织结构变化情况。

关键词: 磁控溅射 , ion-plating , microstructure , plated film

TEM OBSERVATION OF ION-PLATED Al FILM ON Ni SUBSTRATE

WAN Lijun Dalian Maritime University , Dalian , Liaoning , China CHEN Baoqing Dalian Institute of Technology , Dalian , Liaoning , China GUO Kexin(K.H.KUO) Institute of Metal Research , Academia Sinica , Shenyang , China Institute of Metal and Technology , Dalian Maritime University , Dalian , Liaoning , China

金属学报(英文版)

A new phase was found at the interface between Al film and Ni substrate when the time of ion-plating reaches 5 min.It was identified to be body centered tetragonal lattice with the constants a=b=0.588 nm,c=0.480 nm.The variation of microstructure and phases with the ion-plating time were observed.Based on these results,the ion-plating film formation mech- anism has been also discussed.

关键词: magnetron sputtering , null , null , null

MICROHARDNESS DISTRIBUTION AT INTERFACE OF(N~++IP)-TiN COMPOSITE COATINGS ON STEEL

JIN Zhujing YU Li YU Zhiming DAI Shaoxia XU Jiayin Institute of Corrosion and Protection of Metals , Academia Sinica , Corrosion Science Laboratory Academia Sinica , Shenyang , China

金属学报(英文版)

The composite coating of(N~++IP)-TiN was prepared by ion-plated TiN film onto ion-nitrided case on the low carbon steel substrate.The microhardness measurement along in- terface between IP-TiN coating and substrate was detected as a moderate decrease in magni- tude with increase of distance from the coating surface.This seems due to the occurrence of ion nitride case,ε-Fe_3N-Fe_2N and Fe_4N phases,along the interface.

关键词: microhardness , null , null , null , null