Laser direct deposition (LDD) of metallic components is an advanced technology of combining CAD/CAM (computer aided design/computer aided manufacturing), high power laser, and rapid prototyping. This technology uses laser beam to melt the powders fed coaxially into the molten pool by the laser beam to fabricate fully dense metallic components. The present article mainly studies the LDD of Ti-6Al-4V alloy, which can be used to fabricate aircraft components. The mechanical properties of the Ti-6Al-4V alloy, fabricated by LDD, are obtained using the tension test, and the oxygen content of used powders and deposited specimens are measured. In the present article, it can be seen that the mechanical properties obtained using this method are higher than the ones obtained by casting, and equal to those got by wrought anneal. One aircraft part has been made using the LDD process. Because of this aircraft part, with sophisticated shape, the effect of the laser scanning track on the internal soundness of the deposited part was discussed.
关键词:
laser direct deposition
,
null
,
null
金具涛
,
张永忠
,
黄灿
,
石力开
稀有金属
doi:10.3969/j.issn.0258-7076.2009.06.008
采用激光熔化沉积方法制备出Rene95镍基高温合金薄壁样, 分析了沉积态的凝固组织, 并进行了热处理和力学性能测试. 研究表明, 激光熔化沉积Rene95镍基合金的凝固组织为外延生长的定向凝固组织, 其一次枝晶间距在20 μm左右, 二次枝晶臂细小甚至退化, 元素偏析较轻; 通过适当的热处理后, 合金中γ′沉淀相的体积分数明显增加, 合金的显微硬度由沉积态的HV_(0.1) 500提高到HV_(0.1) 540; 经过热处理后, 激光熔化沉积Rene95合金的室温抗拉强度为1247 MPa, 较粉末冶金C级水平略低, 而沿沉积高度方向的延伸率为16.2%, 高于粉末冶金A级水平.
关键词:
激光熔化沉积
,
Rene95镍基高温合金
,
凝固组织
,
力学性能