殷凤仕
,
管恒荣
,
孙晓峰
,
胡壮麒
金属学报
通过液态X射线衍射研究了铸态镍基高温合金M963的液态结构和熔体处理.结果表明：1520℃过热的M963合金熔体中除存在短程有序外, 还有Ni3Al型中程有序原子团簇和残余MC碳化物颗粒；M963合金的熔体结构与其热历史密切相关；与不经任何熔体处理工艺相比, M963合金经1550-1650℃常规熔体精炼后, 975℃/225 MPa条件下的持久寿命和持久塑性明显提高；传统MgO坩埚不能用于1850℃熔体高温处理；采用新研制的具有高抗热震性能的坩埚进行1850℃熔体高温处理M963合金返回料,可显著改善其975℃/225 MPa条件下的持久性能.
关键词:
镍基高温合金
,
liquid structure
,
melt treatment
X.B.Qin
,
S.J.Cheng
,
X.F.Bian
金属学报(英文版)
The structure of Fe-2.0 alloy melt was investigated at 1580, 1560, 1540 and 1450℃ by using an X-ray diffractometer respectively. The results showed that with decreasing temperature, the average atoms of cluster, the coordination numbers, the correlation radius and the atom density increased, whereas the pre-peak of the structure factors curve remained almost at the same position. The appearance of the pre-peak indicated that the liquid structure and the solid structure of the Fe-2.00 alloy were correlated.
关键词:
liquid structure
,
null
,
null
程素娟
,
边秀房
,
张景祥
,
王忠华
,
隋学圃
稀有金属材料与工程
利用回转振动粘度仪在液相线以上较大温度范围内,测量了In-55%Sb(质量分数)亚共晶合金熔体在不同的升降温过程中的粘度.实验结果表明,熔体经历的热历史对其粘度具有显著的影响.熔体在降温过程中的粘度高于升温过程中,在过热100℃后的降温过程中熔体的粘度较之无过热的降温过程中要低.在不同的热过程中,粘度发生转折变化的温度不同,在升温过程中,发生在850℃左右,在过热100℃和无过热的降温过程中,分别发生在750℃和650℃左右.熔体粘度的突变反映了熔体结构在相应温度的突然变化.
关键词:
熔体
,
粘度
,
液态结构
,
热历史
耿浩然
,
王敏
,
邓延波
,
梁伟
稀有金属材料与工程
利用熔体黏度仪系统研究了不同成分Ga-Sb熔体的黏度变化规律.结果表明,Ga-Sb熔体的黏度总体趋势是随温度的降低而增大,黏度变化曲线基本呈指数变化.其中Ga_(36.5)Sb_(63.5)熔体黏度随温度的变化在830℃左右出现突变,将黏度曲线分成低温区和高温区两部分.根据该熔体结构变化的特点,对有关试验结果进行了分析讨论.
关键词:
Ga-Sb熔体
,
黏度
,
液态结构