Bright long afterglow phosphorescence glasses were prepared by using SrAl2O4 : Eu2+, Dy3+ phosphors and suitable glass frits together. The SrAl2O4 : Eu2+, Dy3+ phosphors were initially prepared by the solid reaction method. Three kinds of glass frits were prepared to match the SrAl2O4 : Eu2+, Dy3+ phosphors. Effects of the compositions of the glass frits, the ratios of the phosphors to the frits as well as the firing temperature and firing times on the properties of the samples were discussed. XRD analysis indicated the samples exhibited the typical diffraction peaks of SrAl2O4 : Eu2+, Dy3+. The emission spectra of the samples showed broad bands peaking at 510nm.The excitation spectra of the samples showed broad bands ranging from 300 to 480nm. These are believed due to the 5d4f-4f transitions of Eu2+ in the SrAl2O4 : Eu2+, Dy3+ phosphors. The afterglow luminescence of the samples excited by a 40W fluorescence lamp for 30min can be observed in the dark for more 10h with the naked eyes. It can find wide applications in many fields.
关键词:
long afterglow
,
null
,
null
,
null
李群
,
赵军武
,
孙飞龙
功能材料
首次研究了以Nd~(3+)离子为辅助激活剂,对Eu~(2+)掺杂的发光材料Sr_4Al_(14)O_(25):Eu~(2+)余辉性能的影响.用溶胶凝胶法合成了Eu~(2+), Nd~(3+)共掺杂的Sr_4Al_(14)O_(25):Eu~(2+),Nd~(3+)发光粉末,并用扫描电镜、X射线衍射计、荧光分光光度计、余辉亮度测试仪、热释光剂量计等手段对粉末样品进行了表征.结果表明,在1350℃得到了单一的Sr_4Al_(14)O_(25)相,粉末颗粒平均粒度在1μm左右.Eu~(2+), Nd~(3+)共掺杂的Sr_4Al_(14)O_(25):Eu~(2+),Nd~(3+)发光粉末有402和485nm两个发射峰,与Eu~(2+)单掺杂的Sr_4Al_(14)O_(25):Eu~(2+)相比,发射峰位置没有变化,但适量的掺杂可以大大提高余辉时间和余辉亮度,余辉时间可达18h以上.最后通过对热释光谱的分析解释了双掺杂发光粉余辉性能增强的原因,适宜深度的陷阱可以有效存储光能,增强余辉的时间和强度.
关键词:
Sr_4Al_(14)O_(25):Eu~(2+)
,
Nd~(3+)
,
长余辉
,
溶胶凝胶
,
热释光
袁双龙
,
杨云霞
,
徐志珍
,
方斌
无机材料学报
通过发射光谱、XRD、相对亮度、余辉衰减曲线和热释光谱的测量,研究了在Y2O2S:Eu体系中掺杂Mg2+、Ca2+、Sr2+、Ba2+、Ti4+对荧光体的发光与长余辉特性的影响.结果表明,这些离子的掺杂不影响发射光谱和晶体结构,但显著地影响相对亮度和长余辉特性.它的长余辉衰减过程由一快过程和一慢过程组成,很好地符合指数衰减方程。Mg、Ti共掺杂荧光体的相对亮度和长余辉性能优于单掺杂,与Mg、Ti的含量比有关.根据实验结果,探讨了Y2O2S:Eu体系荧光体的长余辉发光机理.
关键词:
长余辉
,
yttrium oxysulfide
,
dopant
,
mechanism
林元华
,
陈清明
,
张中太
,
唐子龙
无机材料学报
以ＳｒＡｌ２Ｏ４：Ｅｕ，Ｄｙ长余辉发光粉体和低熔点硼硅酸盐玻璃为原料，在一定条件下合成了长余辉蓄光玻璃．研究结果表明，烧成温度和保温时间对该玻璃的发光效果影响较大．温度越高，保温时间越长，由于空气的氧化作用，蓄光玻璃的发光效果越差，本试验控制烧成温度在７５０～８００℃间，保温时间在 １０ｍｉｎ以内，能合成性能较好的蓄光玻璃．余辉衰减曲线表明蓄光玻璃的发光性能较之原始发光粉体有所下降．ＳＥＭ分析表明，低温合成的蓄光玻璃中，所含能继续保持发光性质的粉体料，明显比高温合成样要多．
关键词:
长余辉
,
luminescence powders
,
luminescence glass
,
sinter
杨中服
,
胡义华
,
陈丽
,
王小涓
功能材料
doi:10.3969/j.issn.1001-9731.2014.12.013
使用高温固相法合成了长余辉发光材料Ba3.88-x(Si3O8)2∶0.12Eu2+,xNd3+。实验分别获得了样品的晶体结构、激发与发射谱、余辉衰减、热释光等信息。样品呈现 Eu2+的宽带发射,发射峰位在495 nm,Nd3+的共掺没有引入新的发光中心；Nd3+共掺对材料的荧光强度和余辉强度都有明显的提高,并延长了余辉时间,Nd3+共掺的最优比例为 x=0.04,此条件下材料的肉眼可视的余辉时间从 Eu2+单掺的约20 min延长至1 h；通过对样品的不同等待时间的热释光分析,发现热释光峰位随时间向高温方向移动,过程中半高宽基本不变,对称因子μg 维持在0.52左右,对应的陷阱深度为0.89 eV,陷阱释放载流子的过程可视为二阶动力学过程。
关键词:
长余辉
,
Ba4(Si3O8)2
,
Nd3+
,
二阶动力学
刘兵
,
黄建国
,
刘坐镇
材料导报
主要介绍了长余辉材料的发展历史及其最近的发展概况;以及长余辉发光材料的主要分类,包括硫化物基长余辉发光材料,铝酸盐基长余辉发光材料和硅酸盐基长余辉发光材料等;并对长余辉材料发光机理的模型进行了比较详尽的探讨;同时根据长余辉材料的发展现状探讨了其研究方向和发展前景.
关键词:
长余辉
,
发光材料
,
机理
,
稀土
耿杰
,
吴召平
,
陈玮
,
罗澜
无机材料学报
采用高温固相合成法制得了SrAl2O4:Eu2+,Dy3+长余辉发光材料.X射线衍射分析(XRD)结果表明:该磷光体为SrAl2O4晶体结构,属单斜晶系.其晶格常数为:a=8.4424A,b=8.822A,c=5.1607A,β=93.415°.SrAl2O4:Eu2+,Dy3+发光材料的激发光谱和发射光谱均为宽带谱,激发谱峰位在300～450nm,发射光谱的峰值波长在518nm处.这一结果表明该材料的发光是由Eu2+的4f65d→4f7(8S7/2)宽带跃迁产生的.其余辉衰减由初始的快衰减和其后的慢衰减所组成.通过热释光谱对材料中的陷阱能级进行了分析,该材料中存在两个较深的陷阱能细。苴深度分别为0.38和1.34eV.
关键词:
长余辉
,
spectrum
,
thermoluminescence
,
trap level
林元华
,
陈清明
,
张中太
,
唐子龙
无机材料学报
doi:10.3321/j.issn:1000-324X.2000.06.004
以SrAl2O4：Eu,Dy长余辉发光粉体和低熔点硼硅酸盐玻璃为原料，在一定条件下合成了长余辉蓄光玻璃．研究结果表明，烧成温度和保温时间对该玻璃的发光效果影响较大．温度越高，保温时间越长，由于空气的氧化作用，蓄光玻璃的发光效果越差．本试验控制烧成温度在750～800℃间，保温时间在10min以内，能合成性能较好的蓄光玻璃．余辉衰减曲线表明蓄光玻璃的发光性能较之原始发光粉体有所下降．SEM分析表明，低温合成的蓄光玻璃中，所含能继续保持发光性质的粉体料，明显比高温合成样要多．
关键词:
长余辉
,
发光粉体
,
蓄光玻璃
,
烧成
丁建红
,
李许波
,
黄奇书
,
雷一锋
,
李琼瑛
,
傅汉清
稀土
doi:10.16533/J.CNKI.15-1099/TF.201603017
采用高温固相反应合成了SrAl2O4-yNy∶Eu2+,Dy3+系列长余辉荧光粉,并研究了SrAl2O3.75N0.25∶Eu2+,Dy3+体系的晶体结构、光谱特性、余辉衰减曲线及热释发光曲线.X射线衍射分析结果表明,SrAl2O3.75N0.25:Eu2+荧光材料属六方晶系,P6322空间群,晶胞参数a=b=5.14,c=8.462,γ=120°.荧光光谱测试结果表明,SrAl2 O3.75N0.25∶Eu2+的激发光谱和发射光谱均为宽带谱,激发光谱位于283 nm ～450 nm,发射光谱的峰值位于487 nm,属于Eu2的4f65d1→4f7跃迁发射.Eu2+的掺杂量并不改变SrAl2O3.75N0.25∶Eu2+发射光谱的形状和峰值位置,但对相对发光强度有较大影响,Eu2+的摩尔浓度为2％时相对发光强度最高.余辉衰减曲线表明,Sr0.97 Al2O3.75N0.25∶Eu0.02,Dy0.01的余辉衰减符合指数衰减规律,由初始的快衰减和之后的慢衰减两个过程组成.通过热释发光曲线对荧光材料中的陷阱能级进行计算,得出Sr0.97 Al2 O3.75 N0.02∶Eu0.02,Dy0.01的能级陷阱为0.42 V,掺Dy3+有利于提高该荧光材料的初始发光亮度和余辉时间.
关键词:
铝酸盐
,
稀土
,
长余辉
,
蓝色
,
能级陷阱